海边暴露环境下混凝土抗氯离子渗透性试验研究.pdfVIP

文章编号：1007-046X(2013)06-0036-04 生态建材 海边暴露环境下混凝土抗氯离子渗透性试验研究 Experimental Study of Resistance of Concrete to Chloride Ion Permeability under Sea Environment 1 2 2 马志鸣 ，赵铁军 ，王鹏刚 (1266100 2266033) 摘 要： 对不同配合比的混凝土试件，在海边大气区、潮汐区、水下区进行暴露试验，同时测定氯离子含量随深度 变化曲线。试验结果表明，实际海边暴露环境下混凝土的损伤程度大小为潮汐区水下区大气区，试件内 氯离子含量随着暴露龄期的增加而增加，随时间水胶比的增加而减小。对于水胶比相同的混凝土试件，掺 入粉煤灰等矿物掺合料可以有效提高混凝土抵抗氯离子侵入的性能。 关键词 ： 暴露试验；氯离子；渗透性；耐久性 中图分类号：TU528.2 文献标 志码：A Abstract ：Concrete Elements with different proportion were tested under exposure to sea air zone, tidal zone and underwater environment. Meanwhile, the curves of chloride Ion content with deep change were measured. The result showed that the degree of injury of the concrete sample was tidal zone underwater air zone under sea exposure environment. The content of chloride increased with prolongation of sea exposure period, and depressed in pace with increase of water/cement ratio. The concrete mixed with mineral admixtures such as fly ash could effectively heighten concrete performance on anti-chloride for the sample under the condition of same water cement ratio. Key words sea exposure test; chloride; permeability; durability 0 前 言 在实际暴露环境中氯离子侵入的作用机理，为今后实际工 程中配合比的研发和结构的防护提供充足的理论依据。 氯离子是造成钢筋混凝土中钢筋锈蚀的主要原因，导 致混凝土结构耐久性不足，提前发生破坏，使结构达不到 1 原材料与配合比 设计使用年限。以往对于氯离子的研究仅仅是在试验室环 境下，通过氯离子毛细吸收试验和氯离子自由扩散试验， 　　本试验所采用混凝土原材料均来自青岛本地，试验用 综合评定混凝土结构的抗氯离子侵入性能[1-2] 。然而实际环 配合比为“973 项目”子课题，海洋腐蚀环境下氯离子侵 境中氯离子的作用机理相当复杂，同时与其他因素耦合作 蚀试验研究了项目中的青岛海底隧道所用 4 个混凝土配合 用，加速了混凝土结构的耐久性劣化速率，导致混凝土结 比，研究不同水胶比及不同矿物掺合料对混凝土试件抵抗 构的提前破坏，但对于实际海洋环境中有关氯离子的侵蚀 氯离子侵入的影