圆柱类壳体铸件的金属型铸造工艺.pdf

学兔兔 Apr．2009 铸 造 VoI．58 NO．4 FOUNDRY ·405· 圆柱类壳体铸件的金属型铸造工艺 黄海军 (豫新汽车空调股份有限公司新乡铸造厂，河南新乡453049) 摘要：在理论分析和生产验证的基础上，对内外质量要求较高的圆柱类铝合金壳体铸件，采用金属型铸造的工艺方 法，阐述了在浇冒系统、排气系统、浇注等方面的工艺思想，尤以扁平扇形横浇道和环形内浇道的搭配设计可更加有 效地排渣和热量的分散，效果良好。该工艺方法具有一定的推广意义。 关键词：圆柱类壳体；铸造工艺；金属型铸造 中图分类号：TG249．3 文献标识码：B 文章编号：1001—4977(2009)04—0405—03 Metal Mold Casting Process of Cylindrical Shell Casting HUANG Hai—Jun (Casting Factory Xinxiang，Yuxin Automotive Air Conditioner Co．Ltd．，Xinxiang 453049，He‘nan，China) Abstract：Based on sufficient theoretical analysis and production practice validation，the metaI mold casting process was summarized for cylindrical AI alloy shell-casting，which has high demand for inside and outside quality．Combined with production example，the process ideas on gating and riser system，venting system，pouring technology，etc．were put forward，especially the colIocational designs of flat sector runner and annular ingate which removed the slag more effectively and enhanced the thermal disperse． Key words：cylindrical shell；casting process；metal mold casting 圆柱形壳体类铸件在飞机环境控制系统中占有相 当大的比例，在我厂近几年的新品研制生产过程中也 遇到了很多各式各样的圆柱类壳体铸件，虽然它们在 局部上存在着各式差异，但共同具备的结构特点是， 外形呈圆柱状，两端都有法兰盘结构，一端封闭，一 端开放，铸件要承受1 MPa以下的压力，数分钟内不许 漏气，材料以ZL10I居多。我厂在研制这类铸件的过 程中积累了一些经验，文中将以典型零件HHJ12—135的 图1 HHJ12—135零件结构图 金属型铸造为例加以分析阐述。 Fig．1 Structure drawing ofpart HHJI2—135 1 铸造工艺方案分析 1．1 浇注位置的选择 HHJI2．135壳体的结构见图1。该铸件重量为1．75 kg， 如果采用如图2方案1的放置方向，整个圆弧加工 材料为ZL101，T5处理II类铸件，铸件在机加工后作