海藻酸钠对消失模铸造涂料性能的影响.pdfVIP

学兔兔 海藻酸钠对消失模铸造涂料性能的影响 陈学更，何 龙，李天才，朱劲松 (宁夏共享化工有限公司，宁夏 银川 750021) 摘要：探讨了海藻酸钠对消失模铸造涂料悬浮性、抗弯强度、剪切稀释性、滴淌时间的影响关 系，并与羧甲基纤维素钠进行了对比分析。结果表明，与羧甲基纤维素钠相比，海藻酸钠具有 更佳的增稠效率、更高的强度、更好的涂挂性能和操作效率，并且涂料具有剪切稀释特性和触 变性。 关键词：海藻酸钠；消失模涂料；抗弯强度；剪切稀释性；滴淌时间 中图分类号：TG221 文献标识码：A 文章编号：1673-3320(2014)05—0001—03 Effects of Sodium Alginate on Performance of EPC Coating CHEN Xuegeng，HE Long，LI Tiancai，ZHU Jinsong (Kocel Chemicals Co．，Ltd．，Yinchuan 750021，Ningxia，China) Abstract：With a comparative analysis of sodium carboxymethyl cellulose，the effects of sodium alginate on suspension，flexural strength，shear thinning and dripping time of EPC coating were explored．The results show that compared with sodium carboxymethyl cellulose，sodium alginate has beaer thickening efficiency,higher flexural svength，beaer coating performance and operating efficiency,and the coating has a shear thinning behavior and thixotropic properties． Key words：sodium alginate；EPC coating；flexural strength；shear thinning；dripping time 消失模铸造涂料作为一种特种铸造涂料，与 1 试验方法 消失模铸造一样，在我国的起步较晚。由于对消 1．1 试验原料及仪器 失模涂料的研究还不够透彻，其原材料仅限于一 试 验 原 料 ：海 藻酸 钠 (9 5％ )、铝 些传统砂型涂料的生产原料，涂料配方不成熟， 矾 土 (W(A 1 2 0 3)≥ 9 5％)、二氧 化硅 商品化程度低，指标不能满足高端消失模铸件的 (W(Si0 2)≥99．5％)、白云母 (白度≥8 5％， 生产要求。现阶段，对于国内一些高端的消失模 w(A1 0，)≥60％)、硅藻土、羧甲基纤维素钠 铸造企业，消失模涂料仍旧依赖进口或是一些外 (CMC)、凹凸棒土、白乳胶、有机硅消泡剂、五 资辅材企业的技术引进；对于另外一些相对低端 氯酚钠、氧化铁、Triton X一102、软水。所用原料 的消失模企业，涂料则采用自制白配的方式，严 均为工业级。 重制约我国消失模铸造业的发展f1]。 分析仪器：NDJ一5s旋转黏度计、智能型砂强 近年来，一些水性涂料用新型材料不断涌 度机等。