2006 年用户年会论文 模压成形中模具联接螺栓应力仿真分析 姜年朝，谢勤伟，李湘萍，王克选 ( 南京模拟技术研究所，江苏 南京 210016) [ 摘 要 ]: 针对直升机旋翼桨叶生产中模具联接螺栓的变形和断裂现象，作者应用ANSYS 软件，首次对 桨叶成形模具联接螺栓进行有限元仿真分析，模拟了螺栓在工作过程中的应力变化情况；该计 算方法能够充分考虑螺栓联接的预紧力和固化过程中温度的共同影响，真实地反映实际工况， 为分析这种联接螺栓的断裂提供真实、可靠的数据。同时，分别计算了的单独施加螺栓预紧力 和单独施加固化温度两种条件下应力变化，并进行对比，从而为螺栓设计及桨叶固化工艺提供 一些建议。 [ 关键词 ]: 螺栓预紧力；模压成形；固化；有限元分析 Simulation and Analysis of Stress of Joint Bolt for Die Forming Jiang Nianzhao Xie Qingwei Li Xiangping Wang Kexuan (Nanjing Research Institute of Simulation Technology, Nanjing JiangSu 210016, China) Abstract ：In order to study the reason of fracture and deformation about joint bolt of the die for helicopter rotor blade, simulation and analysis have been carried out with the ANSYS software for the fist time. the changing process of stress about bolt has been simulated. The influence both the bolt pretension stress and the thermal stress during the solidifying have been computed, so this method can explain the reason about bolt fracture. Furthermore, two simulations about the bolt pretension force and the thermal force have been applied to bolt separately and analyzed the influence of two type load. Thus some suggestions are given to the bolt design and solidify techniques. Keywords：Bolt pretension force；Die forming ；Solidify ；Finite element analysis 1. 引言 在模压成形中，螺栓通常是连接上下模具的联结形式。这种联结形式的特点是[1][2][3] ： 螺栓对上下模具施加了预紧力，在模具和螺栓上形成了预应力。在中温或高温固化过程中， 2006 年用户年会论文 这种预应力一直存在，并在温度应力的共同作用下，使螺栓总的应力发生改变。应力的改 变或大或小，当应力超过极限时，从而引起变形甚至螺栓拉断。另一方面，螺栓的变形直 接影响合模缝间隙大小，从而影响产品的厚度。 直升机旋翼桨叶是通过模压成形的。生产出来的桨叶就经常出现翼型变形的情况。在 分析原因时，主要认为是在合模这道工序中，连接上下模具的螺栓由于变形等原因不能起 到正确预紧作用，合模缝的间隙没能够达到预定的大小，