Bi-weekly report.doc

Bi-Weekly report Introduction Two experiments in those two weeks (SEⅡ0042 SEⅡ0043). methods SEⅡ0042(中电半导体): used SEⅡtechnique and phosphorus diffusion as 1.2/57 ohm/□.,printed blue paste with screen of 48 fingers, finger width 0.325, tube PECVD in workshop2. SEⅡ0043(中电半导体): used techniques and phosphorus diffusion was 37.7 ohm/□.,printed blue paste with finger width 0.325, PECVD ran with 75m/h band speed in workshop2. Results SEⅡ0042 Table1 I-V data of SEⅡ0042 Uoc Isc Rs Rsh FF NCell Irev2 #1 0.625 5.295 0.0058 51.909 77.384 0.1639 0.508 #2 0.617 5.142 0.0055 12.131 76.476 0.1553 1.553 #3 0.613 5.233 0.0064 30.778 75.984 0.1560 1.044 #4 0.612 5.233 0.0066 34.749 76.088 0.1559 0.788 #5 0.619 5.287 0.0078 44.493 75.525 0.1582 0.609 #6 0.621 5.241 0.0066 33.886 76.468 0.1593 0.872 #7 0.619 5.225 0.0090 34.987 74.193 0.1536 0.628 #8 0.617 5.220 0.0056 37.451 77.192 0.1591 0.828 #9 0.612 5.089 0.0055 3.222 74.056 0.1475 4.521 #10 0.615 5.211 0.0057 40.942 76.665 0.1573 0.936 #11 0.618 5.157 0.0064 5.548 75.021 0.1530 3.503 #12 0.618 5.282 0.0058 1.211 70.128 0.1465 9.011 #13 0.612 5.023 0.0056 4.206 74.521 0.1466 3.276 #14 0.621 5.217 0.0064 25.684 76.162 0.1579 1.007 #15 0.624 5.328 0.0069 30.248 76.042 0.1617 0.855 #16 0.616 5.205 0.0064 21.420 76.230 0.1563 1.867 #17 0.620 5.254 0.0082 15.988 75.086 0.1567 1.932 #18 0.616 5.121 0.0060 6.494 75.193 0.1517 2.228 avg 0.617 5.209 0.006 24.186 75.468 0.1554 1.998 #19 0.618 4.804 0.0111 8.086 72.109 0.1370 1.961 #9(270) 11(366) #12(252) #13(209) Fig1.1 EL images of SEII0042 #9 #11 #12 #13 Fig1.2 IR images of SEII0042 Fig1.3 QERef of SEII0042 这一批采用了48根栅线，第三道的线宽