热压缩V-5Cr-5Ti合金的Arrhenius本构方程和动态再结晶行为.pdfVIP

Trans. Nonferrous Met. Soc. China 25(2015) 1889−1900 Arrhenius-type constitutive model and dynamic recrystallization behavior of V−5Cr−5Ti alloy during hot compression Yu-fei LI1 2 2 2 1 , Zhen-hong WANG , Lin-ying ZHANG , Chao LUO , Xin-chun LAI 1. Science and Technology on Surface Physics and Chemistry Laboratory, Mianyang 621907, China; 2. China Academy of Engineering Physics, Mianyang 621900, China Received 29 June 2014; accepted 30 October 2014 Abstract: To clarify the high temperature flow stress behavior and microstructures evolution of a V−5Cr−5Ti (mass fraction, %) alloy, the isothermal hot compression tests were conducted in the temperature range of 1423–1573 K with strain rates of 0.01, 0.1, and 1 s−1. The results show that the measured flow stress should be revised by friction and the calculated values of friction coefficient m are in the range of 0.45−0.56. Arrhenius-type constitutive equation was developed by regression analysis. The comparison between the experimental and predicted flow stress shows that the R2 and the average absolute relative error (AARE) are 0.948 and 5.44%, respectively. The measured apparent activation energy Qa is in the range of 540–890 kJ/mol. Both dis-continuous dynamic recrystallization (DDRX) and continuous dynamic recrystallization (CDRX) mechanisms are observed in the deformed alloy, but dynamic recovery (DRV) is the dominant softening mechanism up to a true strain of 1.5. Key words: V−5Cr−5Ti alloy; constitutive model; flow stress; dynamic recrystallization 373