养护剂对高性能混凝土渗透性的影响研究.pdfVIP

学兔兔 江苏建筑 2013年第5期(总第 157期) 养护剂对高性能混凝土渗透性的影响研究 孔祥付．李火星 (江苏博特新材料有限公司。江苏南京2100081 【摘 要】 文章研究了养护荆对高性能混凝土在干燥条件下渗透性的影响。结果表明养护剂可以降低28d碳化深度25．O％ 一 47．3％，降低混凝土表层吸水系数31_3％一89．0％，降低混凝土电通量1．2％一30．0％。养护剂(特别是保水率较高养护剂)对混 凝土表层渗透性的降低作用更为显著。 [关键词】 高性能混凝土；养护；养护剂；渗透性 【中It1~ ]TU528．042 【文献标识码】A 【文章编号】l005—6270(2013)05—0092—02 Research on Effects of Curing Compounds on Permeability of High Performance Concrete KONGXiang--fu LIHuo——xing (Jiangsu Bote New Materials Co．，Ltd，Nanjing Jiangsu 210008 China) Abstract：Effects of curing compounds on permeability of high performance concrete(HPC)under drying were studied in this paper．The results indicated that 28d carbonation depth，surface water sorptivity coefficient and electric flux could be reduced by 25．0％-47．3％，31．3％-89．0％ and 1．2％-30．0％，respectively．Furthermore， curing compounds especially for those with better capacity to reduce moisture loss could reduce permeability of surface concrete dramatically． Key words：hi曲performance concrete(HPC)；curing；curing compounds；permeablility 0 前言 1．1原材料及配合比 养护是混凝土实现其设计性能的最重要因素之一．现 原材料：小野田水泥有限公司生产P·I1 52．5硅酸盐水 代高性能混凝土的特点使养护相比之前更为重要【l】：当今水 泥；南京热电厂 I级粉煤灰；江南$95级磨细矿粉；Elken 泥强度发展速度更快，允许拆模的试件更短．这在一定程度 微硅灰粉：细度模数为2．6的河沙；5 mm 20 mm连续级配 上导致了工程中养护过早地结束：现代混凝土的水胶比较 玄武岩碎石。混凝土配合比如表1所示．通过调节混凝土减 低(特别是对于高性能混凝土而言)，白干燥现象更为显著． 水剂用量将初始坍落度控制在18 cm一20 em。养护剂采用 外部的湿养也很难缓解此现象：现代混凝土工程多掺加矿 江苏博特新材料有限公司生产的Ereducer~201和Ere． 物掺合料，如粉