减水剂对泡沫混凝土性能的影响.pdfVIP

学兔兔 全国中文核心期刊 斩 建筑粉 减水剂对泡沫混凝土性能的影响 管文 [上海市建筑科学研究院(集团)有限公司，上海 200032] 摘要：通过聚羧酸减水剂、三聚氰胺减水剂和萘系减水剂在泡沫混凝土中应用效果的比较表明，萘系减水剂的综合效果最好。 萘系减水剂可提高水泥的分散性及泡沫混凝土的7 d和28 d抗压强度，掺加萘系减水剂后泡沫混凝土的自然干燥收缩率降低，同 时质量吸水率和体积吸水率都呈下降趋势。 关键词：泡沫混凝土；减水剂：孔隙形貌；抗压强度；吸水率；自然干燥收缩 中图分类号：TU528．2 文献标识码：B 文章编号：1001—702X(2011)05—0046—04 The influence of water-reducing agent on performances of foamed concrete GUAN We／2 (Shanghai Research Institute of Building Science，Shanghai 200032，China) Abstract：In this paper，polycarboxylie acid，melamin and polynaphthaene sulphonate water-reducing agent are tested respectively in foamed concrete．The result shows that polynaphthaene sulphonate water-reducing agent has the best comprehensive application effect．It can improve the dispersion of cement and foamed concrete compressive strength of 7 d and 28 d．After dosing polynaphthaene sulphonate water—reducing agent，the natural drying shrinkage of foamed concrete decreased，while nlass water absorption and volume absorption showed a down trend． Key words．．foamed concrete：water-reducing agent~foam pore morphology；compressive strength：water absorption；natural drying shrinkage 0 前 言 1 试 验 泡沫混凝土是用物理方法将泡沫剂水溶液制成泡沫，再 1．1 原材料 将泡沫加入到由水泥、掺合料、骨料、外加剂和水等制成的料 水泥：42．5级普通硅酸盐水泥，上海海螺水泥有限公司。 浆中，经混合搅拌、浇注成型、养护制成的多孔混凝土。由于 发泡剂：褐色液体，复合型泡沫混凝土用发泡剂。 其含有大量封闭孔隙，因而表现出良好的物理力学性能和使 减水剂：聚羧酸减水剂LEX一9，上海市建筑科学研究院： 用功能，具有轻质、耐久、整体性好、施工速度快等优点，近年 三聚氰胺减水剂Melment FIO，巴斯夫化学有限公司；萘系减 来在建筑市场上得到广泛的应用。但目前泡沫混凝土在应用 水剂Mightl00，日本花王化学有限公司。