超轻EPS复合泡沫混凝土性能研究.pdfVIP

学兔兔 2012年第5期 混凝土与水泥制 品 2012 No．5 5月 CHINA CONCRETE AND CEMENT PRODUCTS Mav 超轻EPS复合泡沫混凝土性能研究 杨奉源，卢忠远，何顺爱，牛云辉 (西南科技大学I~tJ Jl省非金属复合与功能材料重点试验室一省部共建 国家重点试验室培育基地，绵阳621010) 摘 要：通过向低水灰比高流动性水泥浆中掺入不同比例的泡沫和EPS颗粒，制备了一系列200 kg／m3超轻 EPS复合泡沫混凝土，并测试了强度、吸水率、软化系数、干缩、导热系数等性能。结果表明，EPS颗粒的引入可以提 高复合体系的强度，降低吸水率，提高软化系数，降低干缩，不会明显影响导热系数，表明EPS可作为制备超轻泡沫 混凝土的优质填充料。 关键词：EPS；泡沫混凝土；强度；吸水率；软化系数；干缩 Abstract：A series di rent ratios of foam and EPS particles has been added to the low water cement ratio paste with high fluidity to prepare a series of 200 kg／m。uhra lightweight EPS foam concrete．The strength，water absorption rate，soft— ening coefficient，drying shrinkage and thermal conductivity of the EPS foam concrete have been tested．It has been ob— served that the addition of EPS particles can improve the strength and softening coefficient，reduced water absorption rate and drying shrinkage，and not significantly affect the thermal conductivity of the composite system，which indicates that EPS could be used as a high-quality filler for preparing ultra lightweight foam concrete． Key wor~：EPS；Foam concrete；Strength；Water absorption rate；Softening coefficient；Drying shrinkage 中图分类号：TU528．2 文献标识码：A 文章编号：1000—4637(2012)05—09—04 0 前言 140～320k~m EPS—FC强度、弹性模量、导热系数的 泡沫混凝土是通过向水泥浆料中引入预先用 影响，结果表明，采用回收破碎得到的EPS颗粒所 发泡液通过物理方式制备的泡沫后制成的气泡均 制备的150-170k~m。密度EPS—FC，导热系数为 匀分布的水泥基多孔材料。泡沫混凝土的密度通常 0．06-0．064W／(m·K)，强度可达0．25-0．28MPa。然而， 在400-1600k~m ，具有隔热、隔音、轻质、调湿、吸 其研究中所用的基体泡沫混凝土密度仅一种，约为 能、吸声、可泵送现浇等多种特性，现已成为建筑节 600k#m。，没有考虑泡沫混凝土密度对EPS—FC强