超长复合型纤维水泥混凝土最佳配合比试验研究.pdfVIP

学兔兔 2011年第l2期 混凝土与水 泥制 品 20ll Nol2 12月 CHINA C0NCRETE AND CEMENT PR0DUCTS December 超长复合型纤维水泥混凝土最佳配合比试验研究 姜丽伟 (哈尔滨工业大学，150090) 摘 要：采用正交试验方法对超长复合型纤维水泥混凝土进行了最佳配合比试验研究。选择水灰比、砂率、纤维 用量和减水剂用量四因素，每个因素四个水平进行试验，并通过极差、均值等分析方法对于正交试验结果进行了分 析，得出了各因素及因素水平的变化对抗折、抗压强度的影响，最后确定了超长复合型水泥混凝土的最佳配合比。 关键词：超长复合型纤维；最佳配合比；正交试验；抗折强度；抗压强度 Abstract：The experimental research of optimal mix proportion is carried out for super—long complex fiber cement concrete by using the orthogonal testing method．Four influencing faetros including water—cement ratio，sand ratio，dosages of fiber and water reducing agent are chosen to conduct the experiment with four levels for each factor．Through different analysis methods such as the range and mean，the orthogonal results has been analyzed，and the effects of each factor and its level changing on the compressive and flexural strength are obtained，and finally the optimal mix proportion of super— long complex fiber cement eoncrete is determined． Key words：Super-long complex fiber；Optimal mix proportion；Orthogonal test；Flexural strength；Compressive strength 中图分类号：TU528．572 文献标识码：A 文章编号：1000—4637(2011)12-38—04 O 前言 合规范要求。 路面水泥混凝土属承受冲击、振动、疲劳、磨损 碎石：1~3cm、1~2cm花岗岩，各占50％。连续粒 的动载结构，其控制技术指标为弯拉强度、耐久性、 级，级配良好。 工作性等。因此，路面混凝土配合比设计必须体现 砂：江砂，级配良好的中砂，细度模数2．4。 路面受力和使用特点【l1。国内外目前尚无一个关于 减水剂：木质素磺酸钙，掺量为水泥质量的 聚丙烯纤维混凝土配合比设计公认程序化的方法， 0．1％～0．7％。 现有的绝大部分方法是在经验以及试验的基础上 超长复合型纤维：长54mm，灰色，单丝／网状双 发展起来的定性的配合比设计方法圜。本文提出的 纤维系统，天然异分子聚合物／聚丙烯，相对密