学兔兔 研究与应用 纤维增强改性水性乳化沥青 防水涂料的性能研究 杨彰堂，李聚刚，陈晓龙 (苏州市姑苏新型建材有限公司，江苏 苏州 215129) 摘要：采用纤维对水性乳化沥青防水涂料进行改性，研究了纤维种类、长度和添加量对改性后涂膜拉伸强度和断裂延伸 率的影响。结果表明，聚酯纤维和聚丙烯纤维适合水性乳化沥青防水涂料的改性，最佳纤维长度为3 mm、添加量为 0．5％ 0．8％，改性后涂膜的拉伸强度和不透水性大大提高，高温性能和粘结强度得到改善，延伸性能会下降但仍能满足 标准要求。 关键词：水性乳化沥青防水涂料；纤维增强改性；拉伸强度；断裂延伸率 。 文章编号：1007—497X(2013)一20—0004—04 中图分类号：TU56 1．65 文献标识码：A Performance Study on Fibre Reinforced Water-based Emulsified Asphalt Waterproofing Coating Yang Zhangtang，Li Jugang，Chen Xiaolong (Suzhou Gusu New Building Material Co．，nd．，Suzhou，Jiangsu 215129，China) Abstract：Water-based emulsified asphalt waterproofing coating was modified by fibre，and this article studied the influences of type，length and dosage of the fibre on tensile strength and elongation at break of the coating．The results showed that polyester fibre and polypropylene fibre were suitable for modification of water-based emulsified asphalt waterproofing coating and the best fibre length and dosage were 3 mm and O．5％一O．8％．The tensile strength and water impermeability of modified coating were improved greatly and the high temperature performance and bonding strength were ameliorated．Elongation performance of modified coating reduced but still met the requirement of standard． Key words：water-based emulsified asphalt waterproofing coating；fibre reinforced；tensile strength；elongation at break 一 般的水性乳化沥青防水涂料具有施工简单便 究，采用纤维对水性乳化沥青防水涂料进行增强改 捷的特点和价格优势，但也因自身强度小而限制了其 性，效果明显。本文研究了纤维种类、纤维长度及添 应用范围。虽然高分子改性的水性乳化沥青防水涂 加量对改性水性乳化沥青防水涂料性能的影响。 料可以达到理想的性能，但价格较高，在实际应