透明硅烷改性聚醚密封胶的研制.pdf

学兔兔 目 建筑密封 透明硅烷改性聚醚密封胶的研制 黄活阳，何晓军，冯炬佳，方铭中 (广东新展化工新材料有限公司，广东 中山 528441) 摘要：以硅烷改性聚醚树脂(Ms树脂)为基料，加入增塑剂、气相二氧化硅、偶联剂、自制催化剂等助剂，制备了一种透明 硅炕改性聚醚密封胶(MS密封胶)。该密封胶固化后拉伸强度为2．93 MPa，断裂伸长率为258％，1 mm厚胶片的透光率 达92％，综合性能较优，能够满足相关标准的要求。 关键词：透明硅烷改性聚醚密封胶；透光率；力学性能 文章编号：1007—497X(2014)一20—0030—04 中图分类号：TU502；TU57 8 文献标识码：A Development of Transparent Silicane Modified Polyether Sealant Huang Huoyang，He Xiaojun，Feng Jujia，Fang Mingzhong (Guangdong Xinzhan New Chemical Material Co．，Ltd．，Zhongshan，Guangdong 528441，China) Abstract：A kind of transparent silicane modified polyether sealant(MS sealant)was developed by taking silicane modified polyether resin(MS resin)as base material and adding plasticizer，fumed silica，coupling agent，self-made catalyzer and other additives．After the sealant cured，its tensile strength and elongation at break can be 2．93 MPa and 258％ respectively，and the light transmittance of a sealant flake of 1 mm thickness is 92％．The overall performance of the sealant is good，and it can meet the requirements of relevant standards． Key words：transparent silicane modified polyether sealant；light transmittance；mechanical property 0 前言 子醚链结构，可提供良好的柔性和高延伸性；而端基 随着建筑装饰工程的不断发展，各式各样的高档 为甲硅烷氧基团，与湿气接触后发生水解缩合反应形 建筑层出不穷。透明密封胶在这些高档建筑的装饰材 成一Si—O—Si一三维空问网状结构。因此，MS密封 料中扮演着重要角色。 胶具有较优的耐候耐久性、粘结性、涂饰性和较高的 自1979年日本开发出硅烷改性聚醚聚合物(MS 抗形变位移能力，同时具有无污染、低VOC含量、易 聚合物)后，以MS聚合物为基料的硅烷改性聚醚密 施工等优点l 3_。透明MS密封胶与透明硅酮密封胶相 封胶(MS密封胶)在欧美等发达国家的大型建筑和高 比，具有更高的透光率和更优的力学性能。然而，对于 端建筑中得到广泛的应用[1-21。MS聚合物主链为大分 透明MS密封胶的研究，国内还停留在理论