经渗硼处理的马氏体时效钢（C-250级）的耐磨性能（英文）.pdfVIP

：全 ：舍 !舍 ： !舍 ： 试验研究 !舍 ! ，；＼：／： ／： 0 BoronizingofMaragingSteel(C-250Grade)：EvaluationofWearBehavior S．C．Heck ，F．A．P．Fernandes，G．E．Totten 。A．LombardiNeto ，L．C．Casteletti (1．UniversityofSaoPaulo，SaoCarlos，Brazil；2．Po~landStateUniversity，Portland，USA；3．Aeroalcool，Franca，Brazil) Abstract：Maragingsteel(250Grade)areusedinapplicationswherehighstrength／weightratio．associatedwith good toughness，arenecessary．These steelsbelongto theclassofhigh strength steels with acombination of 。 strengthandtoughnessthatareamongthehighestattainablebythegeneralengineeringalloys．Surfacetreatments canbeanefficientwaytoimprovethewearresistanceofthiskindofsteels．Boronizingisathermo．chemicalsurface treatmentthatutilizesborondiflusioninto thesurfaceofmetalsandalloystoproducemetallicborides beinga promisingmethodofincreasingthesurfaceperformanceofengineeringcomponentswhilepreserving thesubstrate properties．Inthiswork，amaragingsteel(250grade)wasboridedusingthesaltbathmethod．whatproduceda highhardnesssurfacelayer．Afterboronizing，agreatincreaseinwearresistanceofthissteel incomparisonwith ， un—boridedconditionwasverified． Keywords：maragingsteel；bronizing；wear 经渗硼处理的马氏体时效钢 (C一250级)的耐磨性能 摘要 ：马氏体时效钢 (250级)多用于要求高 的强度 ／重量比及 良好韧性的场合。这种钢属于高强度钢 ，达到 了常用工程合金所能获得的最高的强度与韧性的结合。表面处理可能是改善这种钢的耐磨性的有效 途径。渗硼是使硼渗入金属或合金的表面从而形成金属硼化物的表面化学热处理工艺，既能提高工程 零件的表面性能，又不影响基体性能，是一种具有 良好发展前景的工艺方法。本文对马氏体时效钢 (250级)进行了盐浴渗硼，获得了高硬度的表面层。这种钢经渗硼处理后，其耐磨性能比未经渗硼的 有 了明显的改善 。 关键词：马氏体时效钢 ；渗硼 ；磨损 中图分类号 ：TG156．87 文献标识码 ：A 文章编号：1008—1690(2012)01．0023—04 1 lntroduction 12％ cobahdependingongrade)astheirstrengthening