学兔兔 铸 造 Sep．2011 · 908· FOUNDRY VoI．60 NO．9 C02ti．E化水玻璃砂添加剂及旧砂干法再生工艺 孙鲁洪，楼建余，章 霖 (深圳市景鼎现代科技有限公司，广东深圳518122) 摘要：分析了水玻璃添加剂中有机水溶性高分子和无机纳米材料的组成特性，通过扫描电镜观察CO：硬化水玻璃砂试 样的断口形貌，探讨了水玻璃添加剂的作用机制。生产实践表明，采用水玻璃添加剂并结合旧砂干法再生回用工艺， 可使水玻璃旧砂的回用率达8o％p~上，且型砂工艺性能良好，能满足铸件生产的要求。 关键词：CO 硬化水玻璃砂；添加剂；旧砂干法再生 中图分类号：TG221文献标识码：A 文章编号：i001—4977(2011)09—0908—04 Additive of COrCuring Sodium Silicate Sand and Dry Reclamation Process for Used Sand SUN Lu—hong，LOU Jian-yu，ZHANG Lin (Shenzhen King·Top Modern Hi—Tech Co．，Ltd．，Shenzhen 518122，Guangdong，China) Abstract：The composition features of organic water—soluble polymers and inorganic nano-materiaI in additive were analyzed．The fracture morphology of CO cured sodium silicate sand samples was observed and the function mechanism of the sodium silicate additive was explored．The production practice shows that the reclamation rate of sodium silicate used sand iS over 80％ with the additive of sodium silicate and dry reclamation process．The reclaimed sand has good performance which can meet the requirements of casting production． Key WOrds：C0 curing sodium silicate sand；additive；dry reclamation for used sand 以水玻璃为粘结剂的C02{去造型及制芯工艺自20世 与无机纳米材料构成。以半乳糖和甘露醇为构成单元 纪50年代引入铸造工业以来一直是被广泛采用的型砂 的高分子多糖类聚合体与一种低分子量的水溶性聚合 工艺。CO 化水玻璃砂具有易紧实、操作简单、型芯强 树脂合成后作为添加剂的有机水溶性高分子单元。通 度高等优点；型芯紧实后吹人c0氕体几秒到几分钟就 过阳离子表面活性剂处理的、具有链状和层状过渡结 可以硬化，型芯无需进窑烘干；生产周期短、效率高、 构特征的富镁硅酸盐形成添加剂的无机纳米材料单元。 劳动条件好；型芯在硬化后起模，使得铸件尺寸精确、