Fe－B－C合金冲击磨料磨损性能及磨损机制的研究.pdfVIP

学兔兔 Fe—B—C合金冲击磨料磨损性能及磨损机制的研究 陈 跃，刘赛业，张国赏 (河南科技大学材料科学与工程学院，河南 洛阳471003) 摘要：以高铬铸铁为对比材料，采用MLD一1 0型冲击磨料磨损试验机，研究了Fe—B—c合金冲击磨 料磨损性能；借助于扫描电镜，探讨了Fe-B-C合金的磨损机制。结果表明：Fe—B—C合金的硬度 和冲击韧度与高铬铸铁相当，耐磨性能达到高铬铸铁水平，具有良好的性价比；Fe—B—C合金的 磨损机制是以微观切削为主，同时存在微观断裂和微观犁沟的混合磨损。 关键词：Fe—B～c合金；冲击磨料磨损；磨损机制；耐磨材料 中图分类号：TG142．72 文献标识码：A 文章编号：1673—3320(2010)04—0001—04 Study on Impact Abrasive Wear Resistance and Wear Mechanism of Fe—B—C Alloys Chen Yue，Liu Sanye，Zhang Guoshang (College of Materials Science and Engineering，Henan University of Science and Technology Luoyang 471 003，Henan，China) Abstract：The impact abrasive wear property Of Fe—B—C alloy was studied by using MLD-1 0 abrasive wear testing machine，compared with the same property of high chromium cast iron．The wear mechanism of Fe．B—C alloy was discussed based on the analysis of scanning electron microscope(SEM)． The results show that：First．the hardness，impact toughness and wear resistance Of Fe—B-C alloy are equivalent to that of high chromium cast iron．SO the Fe—B—C alloy has great performance price ratio． Second．the wear mechanism Of Fe—B—C alloy iS a mixed abrasion mechanism，mostly micro cutting，with micro—fracture and micro-ploughing coexist． Kev words：Fe—B—C alloys；impact abrasive wear；wear mechanism；wear resistant materials Fe。B—C合金是近十几年来出现的新钢种，以 碳化物能起到良好的支撑作用，从而使得高铬铸 硼为主要合金添加元素，不加或仅加入微量其它 铁在低应力条件时表现出良好的耐磨性[sI 6I。硼化 合金元素。硼化物 (Fe：B，FeB)本身硬度高， 物硬质相主要由元素硼与铁形成，而硼在基体中 经合适的变质处理和热处理后，能使沿晶界分布 的溶解度非常小，因此，以硼化物为硬质相的耐 的硼化物变成粒状、块状、团球状弥散分布，从