SiC颗粒自增黏熔体发泡法制备泡沫铝铸锭的组织及其特征分析.pdfVIP

学兔兔 有色合金及压铸 S i C颗粒自增黏熔体发泡法制备泡沫铝铸锭 的组织及其特征分析 唐晓亮，刘昌明，张 雷，潘登良 (重庆大学机械工程学院，重庆 400030) 摘要：通过siC颗粒自增黏熔体发泡法工艺制备得到泡沫铝基材料的铸锭；对制得的泡沫铝铸 锭进行各个层面上不同部位的平均孔径和平均孔隙率的测定，得到了铸锭内部的孔隙率和孔径 在铸锭径向和轴向上的变化规律；并且讨论和研究了熔体未发泡区域的形成原因，得到了熔体 直接发泡法制备泡沫材料时气孔的形成过程模型。 关键词：熔体发泡法；SiC颗粒增强；平均孔径；平均孔隙率 中图分类号：TG292 文献标识码：A 文章编号：1673—3320(2009)06—0023—05 Structure and Its Character Analyzing of Al—based Foamy Cast Ingot Fabricated by Molten Frothing Process Using SiC Particles Adhered Melt Tang Xiaoliang，Liu Changming，Zhang Lei，Pan Dengliang (College ofMechanical Engineering，University of Chongqing，Chongqing 400030，China) Abstract：Al—based foamy cast ingot was fabricated by molten frothing process using SiC particles adhered melt．The average pore sizes and porosity rates on every region of the A1．based foamy cast ingot were measured．And according to the measured data on every region changing rules about the average pore sizes and porosity rates in axial and radial directions were obtained．respectively．Then the reason of forming the incomplete foam layer in the ingot was analyzed and discussed．Finally,a model of formation of pores in an ingot when preparing foam material by molten frothing process was gained． Key words：molten frothing process；SiC particles adhered melt；average pore size；average pore porosity 泡沫金属材料尤其是泡沫铝，是新型的高 具有更好的抗变形力和抗拉与抗压强度，可用于 孔隙功能材料。由于泡沫铝独特的多孔结构和金 减振器、吸音器、夹层 (如轻质、渗透材料)和 属特征，使其具备了一般金属无法比拟的优良性 新型建筑材料等。 能，如轻质、高比强度、吸声、隔热、吸收冲击 前期研究对多孔泡沫金属制备工艺研究较 能【1。】等特点，在航空、航天、运输、建筑[4】等领 多，已发表了较多制备工艺研究报告及相关文献 域有广泛的应用前景。 综述[10-12]，但对其组织结构和性能研究较少。随 目前制备泡沫铝的