中频感应电炉脱氧工艺对非金属夹杂物的影响.pdfVIP

学兔兔 Feb．2016 VOl_65 NO．2 中频感应电炉脱氧工艺对非金属夹杂物的影响 李 伟，姜伟航，曹 松，杜天彬，张俊新，王念康 (中车南车戚墅堰机车车辆工艺研究所有限公司，江苏常州213011) 摘要：针对中频感应电炉熔炼的钢中气体含量较高、夹杂物较多的问题，采用复合脱氧剂在炉内以及包内脱氧的工 艺，对钢液进行r脱氧和夹杂物变性处理。试验结果表明，通过复合脱氧后，钢中 [o]含量可降至 (40~60)X104， 同时基本可以消除II、Iv 夹杂物。 关键词：脱氧工艺；气体含量；非金属夹杂物；夹杂物变性 中图分类号：TG243 文献标识码：A 文章编号：1001—4977(2016)02—0172—03 Effect of Medium—Frequency I nduction Furnace Deoxidization Technology on Nonmetallic I nclusion LI Wei，JIANG Wei·hang，CAO Song，DU Tian—bin，ZHANG Jun-xin，WANG Nian—kang (CRRC Qishuyan Institute Co．，Ltd．，Changzhou 21301 1，Jiangshu，China) Abstract：Aimed to solving the problem ofhigh gas content and many nonmetallic inclusion in steel melted by medium．~equency induction furnace． the liquid steel was deoxidated and nonmetallic inclusions were denatured by using compound deoxidant with deoxidization in furnace and foundry ladle and argon bottom．blowing．The result shows that the content of l 0 1 in stee1 can reach (40．6O)xl 0 with complex deoxidization and II．typeIV．type nonmetallic inclusion can removed mostly． Key words：deoxidization process；gas content；nonmetallic inclusion；inclusions modification 随着中同高铁装备走向世界的步伐加快，铁路铸 已成为众多铸造企业急待解决的难题。本文将通过对 造企业为了适应市场的需求，必须开发出一系列高要 我公司中频感应电炉生产铸钢制动元件在复合脱氧工 求的铸钢件。这些铸钢件的材料要求纯净，而钢中气 艺下的非金属夹杂物进行研究，探索中频感应电炉生 体含量及夹杂物常常作为衡量的重要指标。目前，国 产低气体含量、低非金属夹杂物的纯净钢工艺。 内铸造企业在熔炼设备和工艺，尤其在精炼设备及工 1 生产工艺及现状 艺方面与发达国家存在不小的差距，只是用普通的中 频感应电炉炼钢，且大都没有匹配精炼设备，造成的 1．1 制动元件技术要求 结果是钢液纯净度低，钢中气体含量居高不下，夹杂 (1)