低模数水玻璃砂有机酯硬化剂的制备.pdfVIP

学兔兔 造型材料 低模数水玻璃砂有机酯硬化剂的制备‘ 王 美，李远才，张 龙，黄 海 (华中科技大学材料学院，湖北 武汉 430074) 摘要：研究了低模数水玻璃砂 (模数2．0)硬化剂一一有机酯的制备工艺及性能。根据多元醇 醋酸酯的合成工艺原理，实验研究了反应温度、催化剂用量以及多元醇与冰乙酸的摩尔比等对 反应条件的影响，经工艺优化，获得了性能良好的低模数水玻璃有机酯硬化剂——乙二醇醋酸 酯。使用乙二醇醋酸酯硬化剂，能够快速硬化水玻璃砂，并使水玻璃砂具有较好的终强度及低 的高温残留强度。 关键词：低模数水玻璃；有机酯；合成；硬化速度 中图分类号：TG221 ．1 文献标识码：A 文章编号：1673—3320(2009)04—0001—05 Preparation of Organic Ester for Low Module Value of Sodium Silicate SeIf|_hardening Sand Wmag Mei，Li Yuancai，Zhang Long，Huang Hai (School of Material Science and Engineering，Huazhong University of Science and Technology, Wuhan 430074，Hubei，China) Abstract：Preparation of organic ester for lOW module values(m2．0)of sodium silicate self-hardening sand has been studied．Organic ester is synthesized by polyalcohol and acetic acid，and optimized synthesis process has been developed by study the effect of the temperature，the catalyst’S concentration and the molar ratio of acid to polyalcoho1．Ethylene glycol acetate has been prepared by the optimized process，which shows good properties for quick hardening speed，high tensile s~ength and low tensile strength after heating． ’ Key words：low module values of sodium silicate；organic ester；synthesis；hardening speed 有机酯水玻璃自硬砂是一种具有环保优势的 为此，开发一种与低模数水玻璃配套的、其 型 (芯)砂。然而，在有机酯水玻璃自硬砂工艺 加入量最高为水玻璃质量分数的15％，并能达到 应用中出现的最大问题是旧砂再生难度大，有机 正常硬化速度和良好粘结强度的有机酯硬化剂， 酯硬化水玻璃再生砂中的有机酯残留量高，而且 对于解决有机酯水玻璃自硬砂旧砂再生的难题， 随着再生次数的增加，残留有机酯量愈益增多， 具有较大的现实意义。 导致高模数水玻璃旧砂的可使用时间变短。在极 目前用于高模数水玻璃自硬砂的有机酯硬化 端情况下，混好的自硬砂瞬间硬化成为一盘散砂， 剂主要有乙二醇醋酸酯、甘油醋酸酯、二甘醇醋酸 不具备粘结能力。为保证必要的可使用时间，生 酯及其混合物[1]。根据多元醇醋酸酯的合成工艺原