罕见塑料压缩率大全(国外英文资料).docVIP

常见塑料收缩率大全(国外英文资料) Common plastic systolic rate is large Plastic shrinkage Molding shrinkage (molding) refers to the percentage of the size of the original uncooled by the shrinkage of the temperature of the molds when they are removed from the mold and cooled to room temperature. Because shrinkage is not only the heat expansion and shrinkage of the resin itself, but also related to various forming factors, the shrinkage rate of the plastic parts should be called the molding shrinkage rate. This concept is commonly used in polymers. The following are commonly used plastic systolic rates The PA6 series molding shrinkage rate The name and the description of the forming shrinkage rate 15 per cent fiberglass enhancement PA6 0.5-0.8 PA6G15 20% fiberglass enhances PA6 0.4-0.6 PA6 30% fiberglass enhancement PA6 0.3-0.5 PA6G30 40% fiberglass enhancement PA6, 0.1-0.3 PA6G40 50% fiberglass enhancement PA6 0.1-0.3 PA6G50 25 percent fiberglass enhanced flame retardant PA6, 0.2-0.4 z-pa6g25 30% fiberglass enhanced flame retardant PA6 0.2-0.4 z-pa6g30 30% glass fiber reinforced without halogen flame-retardant PA6 0.2-0.4 z-pa6g30 No halogen flame retardant PA6, 0.8-1.2 z-pa6 30 percent of the mineral is filled with halogen-free flame retardant PA6 0.5-0.8 z-pa6m30 30% of glass microbeads fill PA6, 0.8-1.2 PA6M30 30% fiberglass composite filling PA6 0.3-0.5 PA6M30 40% fiberglass composite filling PA6 0.2-0.5 PA6M40 30 percent of the mineral is filled with PA6 0.6-0.9 PA6M30 40 percent of the mineral is filled PA6, 0.4-0.7 PA6M40 PA6 general injection level 1.4-1.8 PA6 PA6 quickly shapes 1.2-1.6 PA6 PA6 generally increases tenacity by 1.5-1.5 PA6 PA6 is moderate-level 0.9-1.3 PA6 PA6 supertoughened 0.9 to 1.3 PA6 MoS2 filling wear-resistant PA6 1.0-1.4 PA6 PA66 series molding shrinkage The name and the description of the forming shrinkage rate 15% fiberglass enhanced pa660-0.9 PA66G15 20% fiberglass enhancement pa665-0.8 PA66G20 25 percent fiberglass enhances heat resistant oil PA6