氧化铝微粉对耐火浇注料性能的影响(国外英文资料).docVIP

氧化铝微粉对耐火浇注料性能的影响(国外英文资料) The effect of alumina micropowder on the properties of refractories The 2010-08-14 Alumina powder was added into refractory castable cold strength, high temperature strength, thermal shock stability, fluidity and the influence of alkali resistance, compares the different manufacturer of alumina powder used in the differences. The results showed that compared with the samples of alumina micropowder, the low temperature and low temperature and alkali resistance were improved significantly. Resistance to thermal shock stability; Low temperature and cold intensity and low temperature intensity; No impact on mobility. The strength of the pouring materials of different manufacturers of alumina micropowder was different, and the application of this formula was based on the excellent mechanical properties of aluminum oxide micropowder B. Zhengzhou jade hair group is Chinas largest producer of white fused alumina, and the establishment of the Shanghai institute of jade hair new research production of many varieties of alpha alumina materials research center. Focusing on white corundum and calcined alpha alumina for nearly 30 years, the focus is professional, contact QQ2596686490, telephone 156390 778. The Al2O3 crystals are: alpha, gamma, eta, delta, theta, kappa, chichi, etc. When conditions change, the crystal changes. In the variation of Al2O3, due to the alpha Al2O3 (density of 3.99 g/cm3), oxygen is the most closely gathering, so only alpha Al2O3 (corundum) is stable, other crystal structure is unstable, will be transformed into alpha Al2O3 when heated. In addition to the corundum, common Al2O3 crystal type shall be the gamma Al2O3, gamma Al2O3 spinel structure, but in its structure, some are not filling tetrahedral gap, thus gamma density of Al2O3 (3.65 g/cm3) smaller than fused alumina. When Al (OH) 3 heating dehydration, about 450 ℃ to form gamma Al2O3, gamma Al2O3 into corundum heated to high temperature. But the shift to above 1000 ℃, the