浇注工艺(国外英文资料).docVIP

浇注工艺(国外英文资料) The name of the company Qingdao haitui machinery co., LTD Pouring process The product name Product material The file number The corporate sector Product drawing no. 1 casting preparation: The casting name, number, weight and pouring order of the cast-type castings 2 check the case of the box, whether the water in the gate is sanded, and there is no need for special handling. 1.3 check if the driving device of the iron water bag works well; The lifting device of the crane is in good condition 1.4 press the suitable pressure for the sand type, and place the position to affect the operation 1.5 pouring channels should be free, no obstacles, no water in pouring, no water in the pouring, and sand in the ground The materials, spherifiers and other alloys that are to be added to the package must be preheated, dried, desiccant and insulation 2 ladle treatment First remove the residue from the iron water bag and clean the bag thoroughly. Coating the wall with a mixture of bentonite and water, increase the viscosity, add the refractory material, the thickness control is 120-150 mm, and the bottom of the bag is strong and seamless. Then add the sand to build the wall of the ladle, and the wall is 50-60mm thick, with a wooden stick, and the wall is higher than the outer rim of the ladle. Make rounded corners to prevent collection gas. Put in the 100 steel tube, make the pouring mouth (teapot), and remove the corners of the ladle, and make a circular arc to prevent the inhale. The ladle repair is complete without damage 2.2 ladle preheating, with log in kerosene fire roasts, require light to take light put, prevent the damage of refractory layer, slowly began to roast, small fire after surface dry, reoccupy fire; To make sure that the ladle is baked and baked, the refractory layer must not be baked and cracked. Before pouring molten iron from the furnace use ladle preheating, after preheating temperature is not less than 800 ℃, ladle lining appear red or dark red,