铝合金材料MIG焊接工艺探析.docVIP

铝合金材料MIG焊接工艺探讨 　　摘 要：焊接铝合金材料中厚板时，常用的焊接方法有TIG和MIG两种焊接方法。如果使用TIG焊接方法，工艺和操作技术比较简单，焊接质量稳定，主要是工作效率非常低。使用MIG焊接方法，焊接工艺复杂，操作技术要求高，焊缝易产生气孔，且熔敷填充金属与母材难熔合，导致焊接质量难于保证，是铝合金材料采用MIG焊接方法的两大难题。但具有比TIG焊接方法高十多倍的工作效率。本文通过探讨分析，实践试验去了解铝合金材料采用MIG焊接方法的焊接性、焊接工艺、操作技术和解决两大焊接技术难点的工艺措施 关键词：铝合金 实践试验 焊接工艺 中国分类号：671.8 文献标识码：A Abstract： Both of TIG and MIG welding methods are always used for thick aluminum alloy steel materials. The practice technique and welding procedure of TIG is simple and the welding quality is stable， but the efficiency is very slow. The practice technique of MIG is very complex and hard， the porosity always comes out in the seams. Deposited metal may be incomplete fusion with base metal and the quality is out of control. These are main difficulties on the thick aluminum alloy steel materials， but the efficiency of MIG is more than 10 times of TIG. This paper analyzes and tests the welding ability， welding procedure and practice technique of MIG for the aluminum alloy steel materials， and puts forward the feasible treatment scheme to resolve the main difficulties. Key words： Aluminum alloy steels； Practical testing； Welding technique 1 前言 进行铝合金材料MIG焊接工艺试验研究，一是为推动焊接操作技术的改进发展，促使新工艺、新技术的高效生产率得以体现，特别是焊接中厚板的工件，采用MIG焊接方法比TIG焊接方法具有非常明显的优势。二是为今后公司承接海工产品、化学品船、LPG、LNG等船舶的建造积累经验和作技术储备 2 研究试验目的 （ 1 ） 通过实践试验，探讨铝合金MIG焊接容易产生气孔和难熔合的问题，如何改进焊接工艺技术，并制定工艺措施，将产生气孔和难熔合的机率降低到许可范围内，确保焊接质量的稳定性； （2）了解铝合金材料在新工艺、新技术中的使用性能，焊接工艺技术； （3）制定正确合理的焊接工艺和操作方法，编制适用生产的工艺规程和技术参数 3 实践试验 3.1 材料性能 铝合金具有良好的耐蚀性，较高的比强度、导电性、导热性及塑性。性能随其纯度的变化而变化，纯度越高，强度越低，塑性越高；另一特点是，随着温度的升高，抗拉强度降低，反之则抗拉强度增高 3.2 工件清洁 铝合金材料焊前工件和焊材经过清理后，应及时施焊，如果存放时间较长，就会新生氧化膜。从清理到焊缝焊完一般在4小时内完成。正常情况下清理工作采用酒精、丙酮等有机溶剂擦拭母材表面附属油污，然后用不锈钢丝砂轮或专用刮刀去除坡口及两侧20 mm范围内的氧化膜，露出金属光泽。不能采用普通砂轮片、钢丝轮、砂纸等作为清理工具，防止在打磨清理中砂粒或其它杂质被压入母材内，而焊接时产生焊接缺陷。尽量不采用机械清理方法，因其对氧化膜的去除不易彻底 采用多层多道焊接时，焊道层间要清洁干净，不允许残留任何杂质。必要时，还要采用刨焊根刀片对焊缝表面进行刨磨，深度为0.5～1 mm 3.3 操作方法 TIG和MIG两种焊接方法，都同属惰性气体保护电弧焊，而高纯氩气是两种铝合金材料焊接方法最常用的保护气体，与其它气体相比，具有引弧容易、电弧电压稳定、保护效果好、导热系数小的特点，最重要是具有