《化学通报》在线预览版 高分子/石墨复合材料的制备与导电性能的研究进展 * 许晶玮 庞浩 胡美龙 廖兵 (中国科学院广州化学研究所纤维素化学重点实验室 广州 510650) 摘要 主要介绍了近年来高分子/石墨复合材料制备方法和导电机理的研究进展。通过氧化、插层以及插层后加热可以在 石墨碳层上引入极性基团，提高其比表面积，有利于高分子进行插层。用处理后比表面积高的石墨制备复合材料可以降 低材料的渗滤值，提高材料的导电性能。复合材料的导电机理可以用渗滤理论来解释。 关键词 石墨插层 导电聚合物 石墨氧化 膨胀石墨 Progresses of Fabrication and Conduction Theories of the Polymer/Graphite Composites * Xu Jingwei, Pang Hao, Hu Meilong, Liao Bing (Key Laboratory of Cellulose and Lignocellulosics Chemistry, Chinese Academy of Science, Guangzhou 510650) Abstract The progresses of fabrication and conduction theories of the polymer/graphite composites have been reviewed. The intercalation of the polymer would be easier and the specific surface of the graphite would be enhanced while the graphite had been pre-processed. The percolation threshold of the composites would be lower and the conductivity would be higher while the graphite had been pre-processed to enhance its specific surface. The way of pre-process can be oxidation, intercalation and heating the intercalated graphite. Key words Graphite intercalation, Conductive polymer, Graphite oxide, Expanded graphite 将高分子材料良好的可加工性和无机导体的导电性能结合起来一直是科研工作者追求的目标之一。 目前主要通过两条途径来实现这一目标，一是制备无机/高分子复合材料来提高高分子材料的电导率，二 是制备含有大的π电子共轭体系的高分子导体。前者通过将无机导体尽可能均匀分散在高分子材料的母 体中，形成导电通路来实现电荷传导。常用的无机导体有石墨、碳纤维等π电子输运型导体，金、银、 铜等金属及其氧化物、碳化物或合金纤维，以及经金属化处理的无机粉末或无机纤维等自由电子输运型 导体等[1] 。目前已经在电子产品中广泛使用的导电橡胶就是通过在硅橡胶等高分子材料中添加碳黑、炭 纤维、金属粉末等材料制成的。后者是一种聚合物本身具有电子导电性分子结构的材料，比如聚乙炔、 聚苯胺等，这种材料一般通过离子掺杂，在高分子链上形成荷电的孤子和极化子，它们在高分子链上的 移动可以传导电荷。本文所要关注的是复合导电材料中以石墨作为填料的材料。 多数高分子材料(共轭聚合物除外)是绝缘体，它们的电导率一般在 10-15~10-20S/cm 的范围内。通过 石墨等导电性物质的掺杂，可以把这些材料的电导率提高到