42.5级硅酸盐水泥的物理性能指标和化学成分(国外英语资料) Physical properties and chemical composition of 42.5 grade Portland cement Questioner: 2011-03-03 08:16 chq111111111 | Views: 4421 Physical indicators: fineness, specific surface area, consistency, setting time, compressive strength Chemical composition: Let me help him with that Satisfactory answer 2011-03-10 19:51 Clay and limestone as raw materials, calcined by high temperature to obtain calcium silicate as the main component of clinker, adding 0 - 5% mixed material and a proper amount of gypsum powder made of rigid cementitious material. The main mineral composition of Portland cement is: calcium silicate three, silicate two calcium, aluminum acid three calcium, iron aluminum acid four calcium. Three calcium silicate cement silicate determines the strength of four weeks; two calcium silicate four weeks to play the role of strength, about one year to reach three four weeks of calcium silicate play strength; strength of aluminum acid calcium three play faster, but the intensity is low, its important role in Portland cement in 1 to 3 day or slightly long time strength; ferritealuminate four calcium intensity is also faster, but low strength, the strength of Portland cement with small. General purpose Portland cement Common, Portland, Cement, cementitious material made of Portland cement clinker and suitable gypsum and specified mixes. Portland cement clinker is mainly composed of CaO, SiO2, Al2O3 and Fe2O3, which is ground into fine powder at the proper proportion and burned to partially molten. The cementitious material with calcium silicate as the main mineral component is burnt. Calcium silicate minerals are not less than 66%, and the mass ratio of calcium oxide and silicon oxide is not less than 2. Referred to as P.O cement strength grade Portland cement strength grade is divided into 42.5, 42.5R, 52.5, 52.5R, 62.5, 62.5R six grades. The strength grades of ordinary portland cement are divided into 42.5 grades: four, 42.5R, 52.5 a