新型智能化焊在钢壁管道上的效用(国外英文资料) The project of high pressure steam pipeline prefabrication, flux-cored wire method was used to get low hydrogen content of weld metal, for the low alloy heat-resistant steel thick wall is particularly important to the weldment. Although the price of core-cored wire is higher than that of solid cored wire, the high welding efficiency and low auxiliary time will reduce the overall welding cost. To tie in with the welding, the introduction of a set of the United States made the MiLLER HDC1500 type pipeline automatic welding machine, and has set up a assembly line layout of pipeline automatic welding prefabrication workshop, chose Beijing ray welding materials, through manual tungsten inert gas welding (GTA W), flux-cored wire gas shielded arc welding (FCAW) filling and cover the welding method for A335 P22 heat-resistant steel pipe welding. 1 material Line 22 mm, specifications for 168 mm material A335 P22 (1 2. 25 Cr mo), equivalent to the domestic material 12 cr2m o. type arc welding power source for the U.S. manufacturing HDC1500 pipeline automatic welding machine, contains the wire feeding system of form a complete set. The specification of the conductive mouth is 1. 2 mm, the nozzle diameter is 20 mm, the rated current is 500 A. Welding process Chrome molybdenum steel thick wall pipe is cut by sawing bed, cutting a 168mm 22mm pipe need 4, 5 min. 1 groove processing adopts pipe groove cutting machine for groove, u-groove. This form of groove can not only be used for the welding nozzle to reach the root of the groove, but also reduce the filling quantity of weld metal. After the processing of the groove, 100% penetration test is carried out according to the JB 4730 2005% pressure equipment nondestructive testing. 2 pipe group pair, bottom and welding Before the piping group is right, the surface of the groove must be used in the surface of the groove and the inner and outer sides of the inner and outer sides of the inner and outer sides. GTA