钛材的应用与失效分析(国外英文资料).docVIP

钛材的应用与失效分析(国外英文资料) Application and failure analysis of titanium material Combined with propylene oxide device of medium corrosive characteristics, the important characteristics of titanium corrosion resistance and one should pay attention to problems in the application of the cyclopropane device of titanium equipment on the actual usage, the failure reasons were analyzed and the measures taken. Divided into highly corrosive hydrochloric acid and strong oxidizing hypochlorite. reaction 1 Overview Titanium has been widely used in recent years as a result of good economic results A new type of engineering material that is widely used, only with a higher ratio The process is as follows: gas reacts with water to form hydrochloric acid and hypochlorite, and chlorine reacts The reaction of chlorate with propene yields allyl alcohol. The whole reaction is mainly in In the alcohol column. In general, the reaction temperature is controlled at 60 ~ At 6 degrees centigrade, it reaches 7 DEG C, and the acid concentration is generally controlled at 5. There are 5 salts Strength, more special corrosion resistance, good mechanical properties And comprehensive process performance. The polyurethane division is produced by the chlorine alcohol process Chloroalcohol reaction system of ring C device technology, due to the presence of strong corrosion Corrosive medium, centrifugal pump for conveying chlorine liquid, and chemical reaction of material From 14% to 16%, alcohol concentration was 38 ~ 42.7.2.%.% chloride. The resulting solution of propanol is delivered by a titanium pump through a titanium tube to a chlorine alcohol feed Preheaters pipe course (process water with 8 steps) and 5 after heating, The lime solution reacts to propylene oxide products. have to The liquid alcohol is hot between the chlorine alcohol tower, the passing preheater and the connection equipment In this process, carbon, aluminum, steel, stainless steel, etc. are not produced Metals can not prevent the corr