一种提高高锰钢性能的新措施 ( ) 浙江科技学院机械与汽车工程学院 3 100 12 　叶岳松 　王瑞金 【摘要】为了提高耐磨高锰钢的淬透性 、抗蠕变性和耐磨性 , 以各合金元素对锰钢性能影响为 依据 ,通过大量的试验 ,提出了高性能耐磨锰钢原料的新配方 , 同时采用冒口加热新工艺和喷 雾淬火新工艺等 ,大大提高了生产效率 ,满足了生产实际对锰钢耐磨性的要求 。 关键词 　高性能锰钢 　配方 　冒口加热 　喷雾淬火 A Ne w Technology to Improve Properties of High Manganese Steel Abstract 　In order to enhance hardenability , creep resistance , resistance to wear of wear resistant material , and as the basis of influence of various alloying element s added to the highperformance manganese steel , a new batch formu la of highperformance manganese steel raw material is p ropo sed through massive experiment s. Meanwhile , a new technology with riser heating and sp ray quenching process are suggested. The result s show that t he p roduction effi ciency is greatly increased and the performance demands of material wear resistant are obtained. Key words 　highp erformances Manganese st eel , batch formula , ri ser heating , sp ray quenching 中图分类号 : T G14272 　　文献标识码 :B 　　耐磨高锰钢韧度高 ,使用中不易断裂 , 安全可 艺 ,实现了提高耐磨锰钢零件使用寿命的研究目标 。 靠 ,特别适用于制造在冲击磨料磨损和高硬力碾碎 1 　各合金元素对高锰钢性能的影响 磨料磨损工况下使用的工件 。如球磨机衬板 ,锤式 破碎机锤头 ,颚式破碎机颚板 , 圆锥破碎机轧臼壁 、 1 1 　磷对高锰钢性能的影响 破碎壁 ,挖掘机斗齿 、斗壁 ,铁道道岔 ,拖拉机和坦克 磷在高锰钢中是有害元素 。磷在奥氏体中的溶 的履带板等 。这些工件的毛坯多数是铸件 ,在浇注 解度低 ,易形成脆性的磷共晶 ,大幅度降低高锰钢的 时 ,往往会因浇注冒口部位冷却速度过快产生缩松 , ( ) 力学性能和耐磨性能 表 1 。磷的含量增加 ,冲击 在机加后的水韧热处理时 ,又容易产生开裂和初始 ( ) 韧性下降明显 表 2 ,将增大钢的冷热裂