批量生产的高磁导率磁芯.pdfVIP

批量生产的高磁导率材料与磁芯 刘九皋 汪作国 杨正忠 邵顺中 摘要：以低ZnO配方和高价离子代换的方法，用普通原料，在真空炉、推扳窑中，按常规烧结 冷却的方式，都可以得到性能优良的R7K、R10K 、R12K 、R15K高μ材料与磁芯器件。在钟罩炉中可 快速烧结出R18K、R20K样环，特别是在功率N2窑中与PC40 材料同烧的R7K、R10K材料ET、EP、RM和环形 磁芯，具有高阻抗、高居里点和良好的 μ-f特性，获得了用户的好评。 关键词 高磁导率 批量 材料 磁芯 High-Permeability Materials and Cores produced by Large-scale Productions Liu Jiugao Wang Zuoguo Yang Zhengzhong and Shao Shunzhong Dongyang Magnetic Enterprise Group Co.of HengDian Group,Zhejiang Dongyang,322118 Abstract ：Using usual raw material,low ZnO content compositions,and substitutional modification by ions with high valence,R7K、R10K、R12K、R15K high- μ materials and magnetic cores with fine magnetic properties can all be obtained in Vacuum-Sintering Kiln and Roller-Kiln,R18K and R20K magnetic cores can also be attained in Bell-Kiln by fast sintering method.In addition,ET、EP、RM and annular cores made by R7K and R10K materials which are sintered simultaneously with PC40 material in the power fettite N2 Roller-Kiln have high impedance、 high Cure temperature and excellent μ-f characteristic,which awarded high reputation from the consumers. Key Words :high permeability,large scale productions,materials,magnetic core 一、引言 随着数字技术和光纤通信技术的发展，电感器、滤波器、扼流圈、宽带和脉冲变压器的普及，电磁 干扰(EMI) 问题日趋严重，在电磁兼容（EMC ）领域，用作抑制电磁干扰的共模扼流圈等元器件发展非 常迅猛。此外，热门话题的节能灯市场磁芯需求量也很庞大。这些应用都促进了高μ材料的飞速发展。 对高μ材料的要求，已不再局限于过去的单纯追求磁导率高，它还必须具有良好的频率特性，即随 着频率的增高，磁导率衰减较慢，阻抗降低较少，当然还必须有较高居里点和良好的温度特性。不断提 高Mn-Zn材料初始磁导率μi这一目标，倾注了磁学界几代人的努力，这是一种迷人的工艺竞赛，也就是 说是一项重要的实践技能。德国人RöESS在 1961 年首次获得μi为 10K而居里点(Tc)仅为 40 ℃的材料， 〈〉 到Tc ＞130℃材料形成产业化大约用了十年时间 1 ，西门子产品目录从 1991 年出现T42( μ12K)到 1997