API 510-模拟试题 原稿.docVIP

ASME SEC.9 OPEN BOOK 1 For corrosion-resistant weld overlay cladding, no open discontinuity exceeding , measured in any direction, shall be permitted in the cladding, and no open discontinuity exceeding 1/8 in. (3 mm) shall be permitted along the approximate weld interface (A) 1/16 in. (B) 1/8 in. (C) 1/32 in. (D) 3/16 in. QW-163 耐蝕覆焊層彎曲試驗開口接受標準為1/16”，一般對焊為1/8” 2 If a WPS is qualified using a base material that is 9 thick, the correct base metal thickness range shown in the WPS should be: (A) 3/16-12 thick (B) 1/16-14 thick (C) 3/16-18 thick (D) 3/16-9.9 thick (E) 3/16-maximum to be welded QW-451.1 3 Two types of impact testing are permitted in ASME IX. One of these is: (A) Charpy V-notch (B) Etch-notch (C) Drop weight (D) Izon notch (E) Either A or C, above QW-170 NOTCH-TOUGHNESS TESTS 4 A welding procedure is qualified on P5A to P5A steel. This WPS is then qualified to weld on: (A) P5A - P4 steels (B) P5A - P5B steels (C) P4 - P4 steels (D) All of the above QW-424 Base Metals Used for Procedure Qualification 5 Which of the following is an essential variable for the GMAW process? (A) A. Wire diameter (B) Travel speed (C) Interpass temperature (D) Electrical characteristics (short arc to spray or vice-versa) (E) Groove design QW-256 WELDING VARIABLES PROCEDURE SPECIFICATIONS (WPS) Gas Tungsten-Arc Welding (GTAW) CLOSE BOOK 1 A welder cannot be qualified by radiography when using: (A) P4X metals (B) P5A metals (C) P3X metals with GMAW-Spray Arc (D) P-1 metals with GMAW short-circuiting arc QW-304 Welders 2 Supplementary Essential Variables (if applicable) must be addressed on the: (A) A. WPS only (B) WPQ only (C) PQR only (D) WPS, PQR and WPQ (E) WPS and PQR only QW-200 GENERAL 3 If the WPS shows a single Vee groove is to be used and the PQR was qualified with a double Vee groove: (A) The WPS can be used without re-qualification (B) The WPS must be requalified (C) The PQR must be retested (D) The WPS must be modified to show the correct joint 開槽方式通常不列入WPS必要變