We make rubber chemicals right TX. C0402001.A.11JAN VulcaPellet®S-80(HD) 预分散台翔药胶®S-80(HD) PRE-DISPERSED POLYMER BOUND COMPOSITION (成份) An exclusive pre-dispersed 80% soluble rhombic sulfur in a 20% elastomeric* (EPDM) / processing aids binder (elastomeric* binder can be SBR or EPDM). 预分散 80%斜方晶硫于20%橡胶弹性载体* *橡胶弹性载体可选择 EPDM或 SBR PROPERTIES (物性) Appearance/外观 Yellow granules/黄色颗粒 3 Specific Gravity/ 比重 (g/cm ) Approx. 1.50 Volatility/挥发度 (80˚C/2hr) 1.0 % Mooney Viscosity/摩尼黏度 (ML 1+4 @ 50˚C) 80 Two year under normal storage conditions/ Storage Stability/储存期 在良好的保存环境下可保存两年 Packing/包装 25 kg per paper bag/25 公斤纸袋 RECOMMENDATIONS AND APPLICATIONS (应用范围及效果) The dispersions of sulfur in NBR (Nitrile Rubber) compounds present well known challenges. Unlike other rubber processing utilizing mill operation, sulfur is recommended to be added at the initial step of mixing. An also common practice is to mix sulfur with NBR in an internal mixer (Banbury or Kneader). So, the operation technique and the temperature and mixing duration control in an internal mixer, need to be carefully articulated. NBR配方中硫磺分散是橡胶工艺中的挑战。在目前 NBR 加工程序中，硫磺无法像其他胶种一样，在 开炼机中添加，必须在密炼机中添加以达到所需的分散性。密炼机打料时间及温度必须谨慎的调整控 制。 General speaking, the Banbury/Kneader mixing time needs to be adequately defined for a satisfied dispersion achievement. Too short mixing time cannot guarantee an optimal dispersion and. longer mixing time may provide the needed dispersion but at the risk and sacrifice of co