镧锶镓镁钴氧化物之合成及其应用于固态氧化物燃料电池电解质材料 .docVIP

中文摘要 本研究主要合成中溫固態氧化物燃料電池之電解質材料，鑭鍶鎵鎂鈷（La0.8Sr0.2Ga0.8Mg0.115Co0.085O3-δ，LSGMC）氧化物，以Pechini 法製備，添加檸檬酸作為螯合配位劑，羥丙基纖維素作為空間分散劑，探討不同比例之檸檬酸與纖維素及不同煆燒溫度對LSGMC相關性質之影響。利用FTIR、TGA/DTA、XRD、SEM、LCR Meter等分析儀器來鑑定前導物之反應機構及生成產物之微結構特性。 研究結果顯示，當檸檬酸/金屬離子莫爾比為3時，斜方晶鈣鈦礦結構的形成溫度可由800 ℃降低至600 ℃，燒結體之相對密度也從81.3 %增加為97.2 %，在650 ℃之導電率約0.015 Scm-1，添加纖維素後導電率增加為0.017 Scm-1，而市售電解質Tosoh-8YSZ在800 ℃之導電率約0.014 Scm-1。由此可知，LSGMC經由適量螯合劑與空間分散劑的添加可使SOFC 操作溫度從800 ℃降低到650 ℃左右，比YSZ更適合作為IT-SOFC之固態電解質。 英文摘要 The perovskite type oxides, La0.8Sr0.2Ga0.8Mg0.115Co0.085O3-δ, as electrolyte materials for intermediate-temperature solid oxide fuel cell were prepared by Pechini method. In which, citric acid was used as a chelating agent, and cellulose was used as a dispersant, to produce the resin of chelate from citric acid and metal ions. The characterization of LSGMC were compared by the analysis of FTIR, TGA/DTA, XRD, SEM, conductivity and density. The results indicated that with the molar ratio of citric acit/metal ions at 3, the forming temperature of orthorhombic perovskite structure decreased from 800 ℃ to 600 ℃, and increased the relative density from 81.3 % to 97.2 %. The electrolyte conductivity of the LSGMC is 0.017 Scm-1 at 650 ℃, which is higher than that of Tosoh-8YSZ (0.014 Scm-1) at 800 ℃. Summary, LSGMC is more suitable for IT-SOFC that can make working temperature decrease from 800 ℃ to 650 ℃. 目錄 中文摘要 ………………………………………………………….. Ⅰ 英文摘要 …………………………………………………………… Ⅱ 致謝 …………………………………………………………… Ⅲ 總目錄 ………………………………………………………….. Ⅳ 表目錄 ………………………………………………………….. Ⅵ 圖目錄 ………………………………………………………….. Ⅶ 第一章 緒論…………………………………………………….. 1 1-1 前言……………………………………………….. 1 1-2 研究動機………………………………………….. 2 1-3 研究目的………………………………………………… 4 第二章 文獻回顧…………………………………………………………… 5 2-1 燃料電池之簡介………………………………………… 5 2-1-1 燃料電池之原理………………………………… 8 2-1-2 燃料電池之優點………………………………… 11 2-1-3 燃料電池之種類………………………………… 13 2-2 固態氧化物燃料電池（SOFC）…………………………… 17 2-2-1固態氧化物燃料電池的優點……………………… 18 2-2-2固態氧化物燃料電池之結構……………………… 19 2-3固態電解質………………………………………… ……… 20