家里给铝合金阳极化的方法 Turn a method of anodizing aluminum alloy at home to someone in need Manual anodizing of aluminium alloys After hard anodizing, aluminum alloy can form a coating with thickness of 30~50 m and hardness of about 500HV, which has excellent corrosion resistance and wear resistance. The scope of application of Aluminum Alloy hard anodic oxidation treatment after widely, involving textiles, bicycles, cameras, pneumatic components, surgical instruments, optical instruments and other industries, is suitable for the cylinder, piston, gear, bearing, impeller, guide, mould engineering components. Heres how to do the anodic treatment at home -- -- I. conditions: aluminum or aluminium alloy must be the anode. Two, equipment: (Wagang, earthen pots can also be, as long as the resistance to acid corrosion, can put down parts on the line) PS: like plastic can. Three. Power supply: 9.6V---12V battery or DC transformer Four, solution: the concentration of 12% sulfuric acid (H2SO4) solution. (for example, 100 ml of solution, sulfuric acid accounts for 12 ml, 88 ml of water), or the electrolyte seems to be available (where the battery is sold to repair the car) Five, stainless steel plate 2 pieces (100mmX100mmX300mm size) Six, several wires; The steps are as follows - The first part thoroughly to the anode removing oil (including fingerprint, hand sweat, dirt and so on) such as using lukewarm water washing powder after scrubbing rinse thoroughly with water, dried. Pour 88% of the tap water into the glass tank, then stir it with a glass bar, and slowly add 12% of the concentrated sulfuric acid, !!! attention!!!! must not put sulfuric acid into the water first, because the concentrated sulfuric acid and water will produce high heat, so that water will boil!!! Very dangerous!!! The amount of solution has been submerged. It is estimated that it will take several hours to cool down to room temperature. When the solution temperature is below 10 degrees Celsius, the hardness of t