厚大断面球墨铸件模拟凝固装置的研制.pdfVIP

张锁梅，闫泽龙，马 瑞 (北京科技大学，北京 100083) 摘要：自行研制了模拟厚大铸件的冷却环境的小型凝固装置。通过控制环境温度和冷却速度，模拟厚大断面球墨铸件凝 固过程温度场的分布和变化规律。试验结果表明，铸件在模拟环境下的冷却凝固时间比空冷凝固时间延长了300％。 关键词：厚大断面；球墨铸件；凝固装置 中图分类号：TF593．2；TG255 文献标识码：A 文章编号：1003—8345(2007)06—0067—04 Development of Apparatus for Sim~ating Solidification of Heavy Section Ductile Iron Casting ZHANG Suo-mei，YAN Ze-long，MA Rui (University of Science And Technology Beijing，Beijing 100083，China) Abstract：A small apparatus used for simulating cooling environment of heavy section ductile iron castings was developed by authors themselves．The temperature distribution field and its variation rule was being simulated by controlling environmental temperature and cooling rate．The test result showed that cooling—solidifying duration of the casting under the simulation environment was~ngthened by 300％ compared with that of air cooling． Key words：heavy section；ductile iron castings；solidification apparatus 厚大断面球墨铸铁由于经过较长的液态冷 1 试验装置 却和共晶凝固，易于导致球化衰退、球墨畸变、石 厚大断面球铁铸件由于冷却速度缓慢，凝固 墨漂浮、缩松、缩孔等缺陷l1l，并且铸件凝固是在 时间长，往往在厚壁中心或热节处出现变态石 高温下的铸型内进行，难以直接观察，特别是大、 墨，常出现石墨球数减少、石墨球径粗大、石墨畸 中型铸件的凝固过程的温度场难以实测，为了实 变、石墨漂浮及晶间碳化物等一系列缺陷，导致 现在实验室环境下研究厚大断面铸件(壁厚超过 厚大断面球铁件性能下降l41。因此可以考虑给铸 100 mm)的冷却凝固过程【2．31，笔者结合厚大断面 件较长的冷却时间，进行人为温度补偿的办法， 球墨铸件的凝固特点，自行研制了能够模拟厚大 使试样的凝固时间远远大于空冷所用的时间，延 铸件冷却环境的小型凝固装置，通过控制不同的 长共晶凝固过程，以此来模拟厚大断面的冷却凝 环境温度和冷却速度，来达到控制铸件凝固速度 固过程l 4l。其试验装置如图1所示。 的目的，以此来获取厚大断面球墨铸件凝固过程 1．1 工作原理 温度场的分布和变化规律，为预测和防止铸件的