鞍 韵 技 术 2016年第5 期 ANGANG TECHNOLOGY 总第401期 ( 生 户 卖 咸 〉 4300 mm厚板线板形缺陷控制 蒋琳 ，冉永亮，，黄松，主勇》壬超，渠秀娟 (鞍钢股份有限公司中厚板厂，辽宁，鞍山，114031) 摘要 ：鞍钢股份中厚板厂4300 mm厚板生产线在生产过程中产生的板形缺陷主要有镰刀 弯和不平度超差。对这两种板形缺陷产生的原因进行了分析，同时提出改进措施，即优化轧制 操作过程和控冷过程^实施后_板形缺陷得到了良好的控制。 关键词：厚板;板形缺陷；控轧控冷 中图分类号：TG335 文献标识码： A 文章编号：1006-4613(2016)05-0057-06 Control of Plate Shape Defects in 4300 mm Heavy Plates Production Line Jiang Lin , Ran Yongliang , Huang Song , Wang Yong , Wang Chao , Qu Xiujuan (Medium and Heavy Plate Plant of Angang Steel Co ., Ltd ., Anshan 114031, Liaoning , China ) Abstract : The major shape defects of a steel plate produced by the 4300 mm Heavy Steel Plate Production Line in Medium and Heavy Plate Plant of Angang Steel Co ., Ltd . includes camber and roughness out -of -tolerance . The causes leading to these two types of defects were analyzed and then such improving measures as optimizing the rolling operation process and controlling cooling process were proposed . After the measures were taken , the shape defects can be controlled well . Key words ： heavy steel plate ; shape defect ; thermo mechanical control process 我国中厚板产量一般占钢材总产量的 10% 进行的重要环节tl]。本文针对4300 n皿厚板线的 左右，被广泛应用于造船、工程机械、容器、能源、 板形缺陷间题进行分析。 建筑等领域，是国民、经济发展所需的重要材料。作 为一个快速发展中的国家，我国对中厚板的需求 1 板形缺陷种类 非常强劲，因此也对中厚板行业提出了更高 在 4300 mm厚板线生产过程中，钢板现货板 的要求D 形经常出现的缺陷有两大类 ，分别是镰刀弯和不 鞍钢4300 mm厚板生产线建于1993年，是 平度趙本文主要针对这两种缺陷进行分析讨论。 国内第一条宽度4 m 以上的中厚板产线，拥有新 1.1镰刀弯 一代超快速冷却系统及|条热处理线，年产量达 图 1 为镰刀弯示意图。图中钢板的宽向两侧 120方 tf产品最太厚度可达150 mm 。产品包括造 呈现弧形的弯曲，i 为钢板的镰刀弯最大值^当镰 船用钢