天铁集团焦化厂脱硫系统改造.pdfVIP

________________________________________又 和 ，r ________________________________________ doi: 10.3969/j.issn. 1006-110X.2016.03.023 天铁集团焦化厂脱硫系统改造 李冬冬 ( 天 津 天 铁 冶 金 集 团 有 限 公 司 焦 化 厂 ，河 北 涉 县 0 5 6 4 0 4 ) [摘要]针对焦炉煤气脱硫系统脱硫效果差、设备腐蚀严重、熔硫系统负荷大等问题，通过对预冷部分、脱硫部分 及硫泡沬熔硫部分进行改造，增强了耐腐蚀性，延长了设备使用寿命，减少了检修量，保证了脱硫系统的正常运行。 [关键词] 脱硫;预冷;溶硫;改造 Modification of Desulfurization System of Tiantie Group Coking Plant LI Dong-dong (Coking P lant, T ianjin T iantie M etallurgy G roup Co., Ltd., She County, H eibei Province, C hina 056404) Abstract In order to address the problem s of poor desulfurization effect and serious equipm ent erosion at desulfurization system an d big load a t sulfur m elting system , m odification w as carried out on p re-co o lin g , desulfurization and sulfur foam and sulfur m elting, im proving erosion resistance, prolonging equipm ent service life, reducing m aintenance an d ensuring the norm al running of desulfurization system. Key words desulfurization; pre-cooling; sulfur m elting; m odification 1 引言 硫 铵 序 。，硫泡沫经泡沫泵输送至熔硫系统，生产 天津天铁冶金集团焦化厂焦炉煤气脱硫系统 硫磺。 承担着 5 5 0 0 0 m 3/ h 焦炉煤气的脱硫脱氰任务。该 2 改造原因 系统采用国内先进的H P F 法脱硫脱氰:工艺。该工: 2 . 1 指标不合格 艺系统由煤气预冷，煤气的脱硫脱氰及硫泡沫熔硫 原系统预冷塔后煤气温度、脱硫液温度过禽. 3 部分组成。 再生器进气量不足、液气比低，脱硫液游离氨含鸶 1 经鼓风机加压后的焦炉煤气先经过预冷塔冷 p H 值偏低，导致脱硫脱氰系统脱硫效果差序后 却 ，煤气从预冷塔下部进人，在预冷塔内经下段焦 煤气含 HjS平均为 4.8 g/Nm3,超 过 20 mg/Nn# 的标 油氨水喷洒除萘降温、上段循环氨水喷洒冷却后， 准要求〇 温度降低为25~30 T d