评价回火引起的硬度分布的变化.pdfVIP

NDTE International 36 (2003) 43–49 /locate/ndteint Evaluation of tempering induced changes in the hardness profile of case-carburised EN36 steel using magnetic Barkhausen noise analysis V. Moorthy*, B.A. Shaw, J.T. Evans Design Unit, University of Newcastle, Newcastle Upon Tyne NE1 7RU, UK Received 27 June 2002; revised 16 September 2002; accepted 16 September 2002 Abstract The effect of tempering on the magnetic Barkhausen noise (MBN) signal profile was studied in case-carburised EN36 steel using a range of magnetic excitation frequencies and a number of frequency ranges for analysis of the MBN signal. The MBN level generally increases with tempering due to coarsening of the microstructure. With higher values of excitation frequency, f EX, the MBN profile exhibits a single peak, but with low values off EX, double peaks are observed. The MBN peak obtained with higher f EX was found to correlate well with hardness changes in a region, down to 100 mm below the surface. The analysis of the MBN signal produced with lowf EX, in narrow frequency ranges selected by software frequency filtering, showed variations in the extent of changes in the relative height of the two MBN peaks in the profile. After taking into account the skin depth-frequency relation for the MBN signal, variations in the values of the two MBN peaks in different analysing frequency ranges were found to correlate well with hardness variations at different depths down to 425 mm below the surface. An empirical relationship has been established between the hardness-depth profile and the MBN measurements. q 2002 Elsev