直读光谱仪光源参数的优化孙建国, 司胜春 摘　要：研究了通过改变预燃时间，火花光源、电弧光源、痕量分析光源的激发时间来缩短激发周期进行中低合金钢分析的方法，通过实验将分析周期从34s缩短到23s，从精密度实验、稳定性实验、结果对照来看该方法是切实可行的，并取得了很好的经济效益。关键词：直读光谱仪；光源参数；分析速度中图分类号：Ｏ657.3　　 文献标识码：B　　 文章编号：1004-4620(2002)02-0055-03 Optimizing the Light Source Parameters of the Direct Reading Spectrometer SUN Jian-guo, SM Sheng-chun (The Department of Insuring Quality of Laiwu Iron and Steel Group Co.,Ltd.,Laiwu 271104,China) Abstract：Through changing the preignition time and the excitation time of sparkle light source,electric arc light source and trace analyzing light source,the method shortening excitation period for analysis of mid of low alloy steel is studied.Through experiment the analyzing period is shortened from 34s to 23s.This method is very good from the results of exactitude experiment,stability experiment and comparison experiment.We have obtained much economical benefit through using this method.Key words：direct reading spectrometer;light source parameter;analysis speed ??? 光电光谱分析具有快速、准确、操作简单和多元素同时分析的特点而被广泛应用于快速分析中。莱芜钢铁集团股份有限公司炼钢厂（简称莱钢炼钢厂）为降低炼钢生产成本、提高产品质量并做到成分可控，将浇铸过程中取样改为吹氩后取样快速分析，成分合格后再浇铸，这就要求化验室需在尽可能短的时间内报出分析结果。化验室的分析速度直接影响炼钢的生产成本，分析时间每降低1s，可以减少因炉衬浸蚀、电耗以及其它生产费用约合人民币1元。为此，需研究如何缩短分析周期，提高分析速度。以中低合金钢的快速分析为例，对中低合金钢来说，合金元素含量较低，并且绝大多数合金元素不做分析要求，为此研究了通过改变预燃时间，火花光源、电弧光源、痕量分析光源的激发时间来缩短激发周期。应用该方法对中低合金钢进行分析，实验结果令人满意。 1 实验部分 1.1 仪器与设备??? (1)SPECTROLAB M8直读光谱仪?　 光学系统：1个N循环密闭真空室、2个空气室??? 软件：SPECTROLAB M8操作软件??　 光源：包括Presp、Spark1、Spark2、SAFT、Arc、PIMS等放电方式，可通过软件进行设置。??? (2)光谱磨样机1.2 分析条件??? 氩气：纯度≥99.99%? 氩气压力：0.6MPa? 氩气流量：光源开：20L/h；光源关：10L/h　对电极：钨棒90°锥角，极距 3mm1.3 样品　标准化样品：随机标准化样品RN13、RN14? 类型标准化样品：K20MnSi、Az、45#? 标准样品：GSBH40078-94-S9254-S9259? 生产样品1.4 分析方法　　选用Fe-10中低合金钢分析程序。　标准化：用随机标准化样品RN13、RN14对曲线进行标准化。　类型标准化：用自制控制样品对曲线进行类型标准化。　样品分析：利用已类型标准化的曲线进行样品分析。 2 结果与讨论 2.1 预燃时间的选择　在其它光源条件不变的情况下将预燃时间从1s开始依次增加1s，分别测定比强度值，共测定10次，结果见表1。从测定结果可以看出预燃7s以后比强度趋于稳定，将预燃时间设定为8s。 表1 不同预燃时间的比强度测定值 预燃时间/s C Si Mn P S Cr Ni Cu 1 43626 7141 163825 4702 8860 3026 855