bi2 o32li2 o 玻璃的热致变色研究3 - researchgate.pdf

See discussions, stats, and author profiles for this publication at: /publication/265551826 Study on the thermochromic properties of Bi2O3-Li2O glasses Article in Acta Ph sica Sinica -Chinese Edition- · Januar 2001 CITATIONS READS 0 16 1 author: Danping Chen Shanghai Institute of Optics and Fine Mechanics, CAS 271 PUBLICATIONS 4,041 CITATIONS SEE PROFILE Some of the authors of this publication are also working on these related projects: Femtosecond laser micro/nano-machining View project Laser fiber View project All content following this page was uploaded b Danping Chen on 15 December 2015. The user has requested enhancement of the downloaded file. 第 50 卷 第 8 期 2001 年 8 月 物 　理 　学 　报 Vol. 50 ,No. 8 ,August ,2001 ( ) 10003290200150 08 150106 ACTA PHYSICA SINICA 2001 Chin. Phys. Soc. Bi O Li O 玻璃的热致变色研究 2 3 2 陈丹平 　姜雄伟 　朱从善 ( 中国科学院上海光学精密机械研究所,上海　201800) ( ) 2001 年 1 月 18 日收到;2001 年 3 月 19 日收到修改稿 　　发现氧化　和氧化锂所形成的玻璃有着明显的热致变色现象. 温度系数随氧化　含量的增加而上升 ,反映了 热致变色现象主要来源于氧化　. 这种热致变色现象与半导体同样 ,来源于玻璃中的电子声子相互作用而产生的 随温度变化的光学能隙. 氧化　重金属氧化物玻璃中高电子密度和低声子能量的化学键是产生强电子声子相互 作用的主要原因. 关键词 : 玻璃 , 热致变色 , 电子声子相互作用 PACC : 4270C , 7820W , 6320K 氧化物玻璃结构的了解. 另外 ,玻璃的非线性光学 1 　引 言 系数是其光学能隙的函数 ,光学能隙越窄 ,非线性光 学系数就越高 ,所以关于玻璃的光学能隙随温度变 以Bi O 为代表的一类重金属氧化物玻璃近