铅黄铜零部件表面除铅处理.pdf

李昆仑等 　铅黄铜零部件表面除铅处理 铅黄铜零部件表面除铅处理 李昆仑 , 王 　疆 , 沃银花 , 郦 　剑 , 王幼文 (浙江大学材料科学与工程系 ,浙江 杭州 310027) 　　[摘 　要] 　研制了一种用于铅黄铜零部件表面除铅溶液 ,并开发了与之相关的黄铜零件表面除铅工艺 。X 射线能谱 分析证明 ,经表面除铅处理后的黄铜零件表面的含铅量 ,低于标准规定值 。 [ 关键词] 　铅黄铜 ;铅中毒 ;水污染 ;除铅 ( ) [ 中图分类号] 中图分类号 :TG178 　 　 　 [文献标识码]A 　 　 　 [文章编号] 1001 - 3660 2005 02 - 0046 - 03 Study on a Leadleaching Technique of Brass Components L I Kunlun , WAN G J iang , WO Yinhua , L I J ian , WAN G Youwen ( School of Materials Science and Engineering , Zhej iang University , Hangzhou 310027 , China) [ Abstract ] A sort of leadleaching solution used for cleaning out the lead on the surface of leadbrass compo nents has been developed successfully . The operating process is designed correspondingly . Demonstrated by EDS anal ysis , the surface lead content of the components which had been treated by this leadleaching solution is reduced un der standard value . [ Key words ] Leadbrass ; Leading poisoning ; Water pollution ; Leadleaching 0 　引　言 实研采用特殊化学药品配制成除铅溶液 ,通过化学反应使 零部件表面的铅组分溶解 ,达到清洁表面的目的;在除铅溶液中 随着生活水平的提高 ,人们对 自身的健康问题越来越重视 。 加入适当的抑制剂 ,保护铜锌免于溶解 。铅在大多数无机酸中 在我国 ,生产饮用水系统零部件多采用铅含量为 2 %～3 %的铅 生成表面附着力较强的物质 ,溶解度极低 ,所以脱溶性较差 ; 同 黄铜材料 , 以利用铅的润滑作用 ,提高表面质量 , 降低成本 。但 样在许多碱中 ,亦生成溶解度极低的保护膜 ,脱溶性也不好 。但 是 ,铅黄铜管道和阀门表面的铅 ,会随着水的冲刷 、浸泡或与水 铅在一些有机酸中却有较大的溶解度 ,尤其在有一定的催化剂 中的其它物质发生反应而进入水中 ,被人体摄入 。医学研究表 存在时 ,溶解度可以大大地提高[3 - 4 ] 。因此可以考虑采用此类 明 ,如果摄入铅的量超过标准 ,会影响人体造血功能、神经系统