WCCo硬质合金γ相相变.pdfVIP

稀有金属000205 稀有金属 CHINESE JOURNAL OF RARE METALS 2000　Vol.24　No.2　P.101-105 WC-Co硬质合金γ相相变 刘寿荣 摘　要：　通过X射线衍射相分析和应力分析研究了WC-Co硬质合金γ相 (钴基Co-W- C固溶体) 的相转变。 WC-Co硬质合金在烧结后至室温的冷却过程中γ相以扩散型机 制为主进行fcc→hcp相变， 其非扩散型的M 转变点在室温以上并接近室温， 室温下烧 s 结态合金中hcp含量很少。 在M 点以下， 凡引起合金中WC相与γ相间内应力变化 (加 s 强或松驰) 的工艺因素均能导致合金γ相中hcp γ相比例的增加。 关键词：　WC-Co硬质合金　γ相　相变 文献标识码：　A 文章编号：　0258-7076(2000)01-0101-05 Binder Phase Transformation in WC-Co Cemented Carbides Liu Shourong （Tianjin Institute for Hard Alloy, Tianjin 300222, China ） Abstract ：　The binder phase (Co-W-C Solid Solution) transformation in WC-Co cemented carbides was studied by means of X-ray diffraction. The results show that the fcc→hcp transformation of γ-phase is mainly a diffusive type when cooling WC-Co samples above room temperature; the nondiffusive martensite transformation temperature (Ms point) of γ- phase approaches and is above room temperature; any factors resulting in strengthening or lossing the internal stress between WC rigid skeleton and γ-phase below Ms point are all the reason why the amount of hcp γ-phase increases. Key Words:　WC-Co cemented carbides, γ-phase, Phase transformation 　　关于WC-Co硬质合金γ相的结构及其相转变的研究， 国内外有较多成果发表 ［1～ 6］ ， 但不同作者的研究结果不尽一致。 国内许多作者给出的烧结态WC-Co合金室温 下hcp γ相含量明显偏高 (多达40%)， 有的作者认为高钴含量合金中hcp γ相比例较低 ［1］ 钴合金为高； Кудрявцева等 称烧结态WC-20 Co合金中的γ相都是fcc ［2］ 认为由于WC刚性骨架对γ相的“机械约束作用”造成了WC-Co合金的 型； Exner ［3］ 则认为钨在钴中 fcc γ相更加稳定， 从而室温合金中γ相都是fcc型的； Giameia等 钴， 接近1000 K， 但钨在钴中的固溶却使其非扩散型的fcc γ→hcp