高交联度易加工硅烷交联管材专用料的研制.pdfVIP

第36卷增刊 塑料工业 2008年6月 CHINA PLASnCS INDU 汀RY 高交联度易加工硅烷交联管材专用料的研制 张 瑞，逯翠霞 (大庆化工研究中心，黑龙江 大庆163714) 摘要：介绍了采用二步硅烷交联工艺制备高交联度易加工硅烷交联管材专用料的方法，讨论了基础树脂、助剂对 专用料交联度和加工性能的影响；通过加入自由基捕捉剂的方法，抑制接枝反应过程中的碳一碳大分子交联，解决了 二步法硅烷交联领域的技术瓶颈问题，使硅烷交联管材专用料既具有高的交联度又具有良好的加工性能。 关键词：硅烷交联；管材；自由基捕捉剂；加工性能；交联度 Development of High Crosslinking and Easy Processable Silane Crosslinked Pipe ZHANG Rui，LU Cui—xia (Daqing Research Center of Chemical Eng、，Daqing 1637 14，China) Abstract：The method for the preparation of high crosslinking and easy pl~)cessable pipe compound by two—step silane crosslinking Was introduced．The effects of basis resin and additive on the crosslinking degree and process— ability of the compound were discussed．The technical pinches in the two—step silane crosslinking were solved by the addition of radical scavenger into the base resin to inhibit the macromolecular crosslinking during graft reaction， making the compound having high crosslinking degree and excellent processability． Keywords：Silane Crosslinking；Pipe；Radical Scavenger；Processability；Crosslinking Degree 硅烷交联技术是聚乙烯 (PE)改性的重要手段 子构成调整剂 (F一1)：大庆石化公司；引发剂 DCP： 之一，交联后的PE由于形成了网状结构，显著地提 哈尔滨化工研究所；硅烷接枝液A一171：哈尔滨化工 高了耐热性能、耐老化性能及高温下的力学性能而广 研究所；催化剂：北京化工三厂；自由基捕捉剂：自 泛应用于电力电缆行业、供热管道及油田中的输油管 制。 道E1～ 。 1．2 分析方法 硅烷交联管材专用料的关键是产品既要有较高的 凝胶含量的测定：准确称取0．2～0．3 g交联PE， 交联度 (165％)以保证形成较完整的交联网络具有 样品恒重后，将其包入滤纸内，外包120目的钢网， 优良的热性能及力学性能，同时还要具有良好的加工 构成试样包，直接放人以二甲苯为溶剂的回流装置 性能，使成型的管材具有光滑的内外壁，以免形成应 中，回流萃取8 h，萃取完毕后取出试样包，放入烘 力开裂点。而加工性能好和高交联度这一矛盾问题一 箱中在110 oC下烘4 h，再放入干燥器内冷却30 min， 直是二步法硅烷交联领域的技术难题，要想达到较高