刘芳-利用磷矿渣制碱矿渣胶凝材料研究.pdfVIP

利用黄磷炉渣配制碱矿渣胶凝材料的研究 刘芳 王冲 吴建华 重庆大学材料学院 重庆市，400045 ，邮箱:xiaoliu@yeah.net，电话 Material Science and Engineering College,Chongqing University,Chongqing, China. 400045 摘要：通过试验研究了利用黄磷炉渣配制碱矿渣胶凝材料的技术，将磨细黄磷炉渣、磷 石膏与少量水泥熟料混合，利用适当配比的氢氧化钠、硫酸钠、铝酸钠和磷石膏作为复 合碱性激发剂，可制得强度等级达到 42.5MPa 的碱矿渣胶凝材料。研究了不同外加剂对 碱矿渣胶凝材料不同龄期时的抗压强度、抗折强度影响。 关键词：黄磷矿渣；碱矿渣胶结材料；碱性激发剂；潜在活性 Abstrac ：The technique producing alkali-slag cementitious material used phosphor slag had been studied. Mixing ground phosphor-slag and phosphogypsum with a small quantity of clinker, using sodium hydroxide, sodium sulfate, sodium aluminate and phosphogypsum in appropriate mixture ratio as multiple alkali-active agent, the alkalic-slag cementitious material with 42.5MPa strength grade can be made of. The influencing of different agents to the compressive strength and flexure strength in different ages had been studied. Key words: phosphor slag, alkali-slag cementitious material, alkali-active agent, potential activity 中图分类号：TU528.1 0 前言 黄磷炉渣是黄磷厂排放的工业废渣：每生产一吨黄磷要排放 8～10 吨的 黄磷炉渣，目前我国黄磷炉渣的排放量达 200 多万吨，长期以来未得到有效 利用，作为工业废渣堆积如山。由于黄磷渣中含有少量的磷酸根离子和氟离 子，在雨水中会逐渐溶解而渗入在下，严重污染环境。 黄磷炉渣是利用磷矿石生产黄磷后的工业副产品，在冶炼过程中，处于 熔融状态下的磷渣经水淬而冷却，经分析其中的主要成分是硅酸盐玻璃体， SiO2和CaO总含量近 90 ％，具有潜在的水化活性。但由于其中同时含有一定 量的磷酸根离子和氟离子，若不采取一定措施，当磷矿渣掺量到一定比例后， 所制的胶凝材料凝结时间过长，早期强度过低，无法作为正常的胶凝材料使 用。 碱矿渣胶凝材料是利用碱金属化合物作为碱组分，激发黄磷炉渣的的潜 在活性，使其水化硬化而得到的一种水硬性胶凝材料。 鉴于上述情况，本文研究了利用黄磷炉渣制碱矿渣胶凝材料的工艺及其 相关性能。 1 实验 1.1 原料 水泥熟料：重庆地维水泥厂硅酸盐水泥熟料，其化学成分见表 1； 磷 石 膏：贵州息烽磷业公司工业废渣，其化学成分见表 2； 黄磷炉渣：贵州息烽磷业公司工业废渣，其化学成分见表 3； 水玻璃：模数为 2.4，相对密度为 1.40； 砂：重庆渠河砂； 固 态 复 合 碱 性 激 发 剂 ： 采 用 市 售 化 工 原 料 自 制 ， 主 要 成 分 为 Na SO ,Na CO ,NaOH,NaAlO ,Na SO 等。 2 4 2 3 2 2 4