钯纳米线的制备及其在乙醇燃料电池中的应用 - 中国科技论文在线.pdf

中国科技论文在线 钯纳米线的制备及其在乙醇燃料电池中的 应用 代相成* （安徽大学化学化工学院，合肥 230039 ） 摘要：以阳极氧化铝为模板制备了具有高度有序微观结构的金属钯的纳米线。扫描电子显微 镜（SEM ）分析表明，钯纳米线直径为50nm，且直立于电极表面。循环伏安扫描表明，在 碱性环境中，钯纳米线对乙醇电氧化具有很高的催化活性。起峰点位在-0.58V，峰电流密度 达到89.6mA/cm2，正扫时的峰很尖锐，说明随着电压的升高，电极表面的乙醇被迅速消耗， 因而钯纳米线对乙醇催化有很高的活性。 关键词： 醇类燃料电池；钯；纳米线 中图分类号：TB33 Preparation of palladium nanowires and application in ethanol fuel cell Dai Xiangcheng (College of Chemistry and Chemical Engineering, An hui University, Hefei 230039) Abstract: Metal palladium nanowires with highly ordered microstructure was prepared by anodic alumina. Scanning electron microscopy (SEM) analysis showed that the diameter of the palladium nanowire is 50nm, and upright on the electrode surface. Cyclic voltammetry showed that palladium nanowires has a high catalytic activity to the ethanol electro-oxidation in the alkaline environment. The peak point is located at-0.58V, the peak current density is 89.6mA/cm2, The peak is very sharp, shows that as voltage increases, the alcohol on electrode surface was rapidly consumed and thus palladium nanowires have high catalytic activity. Key words: Alcohol fuel cells;palladium;nanowires 1 引言 直接醇类燃料电池由于燃料不用经过重整而直接用于发电因而具有高理论比能量密度 和极高的发电效率[1.2] 。近年来，直接乙醇燃料电池(DEFCs)受到了广泛的关注，其电极催化 材料多用Pt 以及各种Pt 基合金[3-4]，但是在乙醇催化氧化过程中，所产生的中间产物CO 会 强烈地吸附在Pt 催化剂上，使其被毒化，降低其活性[5-6] 。最近的研究表明，在碱性环境中 Pd 对乙醇的氧化具有比Pt 更高的活性[7-9] 。本文以阳极氧化铝为模板，制备了具有高度有序 结构的钯纳米线，并应用于乙醇电氧化中。利用纳米材料巨大的表面积和较高的催化活性， 取得良好的催化效果。 2 实验部分 2.1 装置与试剂 PARSTAT2273 电化学工作站（美国阿美特克有限公司）、INSTEK GPR