石蜡 膨胀珍珠岩复合相变材料的制备 李海建.pdfVIP

实验与研究 石蜡/膨胀珍珠岩复合相变材料的制备 Preparation of paraffin/expanded perlite composite phase change materials 李海建冀志江辛志军王静 （中国建筑材料科学研究总院绿色建筑材料国家重点实验室， 北京 100024） 摘要：利用真空吸附法制备了石蜡 膨胀珍珠岩复合相变材料，此相变材料经过差示扫描量热仪、扫描电镜和扩 / 散 渗出圈法测试，结果显示此相变材料具有调温功能，石蜡被吸附到膨胀珍珠岩孔道中并且分布均匀，性能稳 － 定，可以应用到建筑材料中。 关键词真空吸附法 复合相变材料 石蜡 膨胀珍珠岩 : ： Abstract Paraffin/expanded perlite composite phase change material (PCM) was prepared using the method of vacuum absorption and tested by means of differential scanning calormetry (DSC) , scanning electron microscopy (SEM) and dif - fused-exudative circle method. The testing results show that paraffin was absorbed into the holes of inorganic carriers completely and distributed evenly with stable performances. It is concluded that the composite PCM has steady tempera- ture-adjust function and the PCM may be applied in building materials. Key words: vacuum absorption, composite phase change material, paraffin, expanded perlite 中图分类号： 文献标识码： 文章编号： （ ） TU55+1.34 B 1003-8965 2009 03-0069-03 1 前言 孔介质作为有机相变物质的储藏介质是近年来在 相变储能技术领域出现的一种新的有机相变物质 随着我国经济发展和人民生活水平的提高 我 封装方法，这种方法简单易行，制备的复合相变材 , 国建筑能耗增长迅速 统计数据显示 年我 料性能稳定。 , , 2004 国建筑总面积为 389 亿平方米， 建筑能耗占社会 本文采用真空吸附法，在实验的不同反应阶段 控制不同的压力来制备石蜡 膨胀珍珠岩复合相变 总能耗的25.5%, 建筑节能刻不容缓，在国务院批