维普资讯 第30卷第1期 工 业 炉 Vo1．3O No．1 2008年 1月 Industrial Furnace Jan．2008 60万t高速线材加热炉的技术设计 童庆年，孙秀成 (马钢 (合肥)钢铁有限责任公司设备部，安徽合肥230011) 摘 要：马钢(合肥)公司高速线材全梁式步进加热炉设计生产能力为冷装100 t／h，热装130 t／h，燃用高、焦混合煤 气，煤气热值为l 800x4．18 kJ／m’。加热炉从设计、施工、烘炉总体质量优良，生产指标达到设计要求。 关键词：步进加热炉；设计；技术特点 中图分类号：TG307 文献标识码：B 文章编号：1001—6988(2008)O1．0020．03 Technical Design to the Reheating Furnace of High-Speed Wire Plant of 6OO ooO Tonnes TONG Qing-nian，SUN Xiu-cheng (Equipment Department in Ma’anshan(Hefei)IronSteel Co．Ltd．，Hefei 23001 1，China) Abstract：The essay introduces the walking beam reheating furnace of high spead wire plant in Ma’ anshan(Hefei)Iron＆Steel Co．Ltd．Its design capacity is 1 00 t／h for cold-charging and 1 30 t／h for hot— charging,its fuel is the mixed gas between blast furnace and coke ovea gas with heat value of 1 800x4．1 8 kJ／ m3 the production indexes of reheating furnace have reached the designed requirements and its whole quali— ty is good from design，constraction to baking furnace． Key words：walking beam reheating furnace；design ；technical characteristics 马钢(合肥)钢铁有限责任公司高速线材生产线 cI=，加热炉支撑水梁绝热完好时，冷装 1212 kJ／kg 于2006年9月 18 Et动工新建．年设计产量60万 坯，热装878 kJ／kg坯。 t，加热炉为全梁式步进加热炉，加热炉设计生产能 (2)氧化烧损 力为冷装 100 t／h，热装 130 t／h。坯料为：150 mmx 正常情况下，烧损不大于0．75％。 150 mmxl2 000 mm标准坯．产品规格为 ～13 mm (3)有效炉底强度 光面圆钢盘条和螺纹钢盘条。加热钢种为碳素结构钢． 500～600 kg／(h·m )时，能耗和投资较佳。 燃料为高焦混合煤气，热值为1 800x4．18 I(J／m。。平 (4)坯料加热时间 均坯料热装温度I600 cI=，热装率≥80％。2007年3 67．5 min，单位厚度加热时问为4．5 min／cm。