CO2激光焊接AZ31B变形镁合金中的等离子体光信号检测和熔透状态识别.pdfVIP

Plasma light emission monitoring and penetration status recognition in CO2 laser welding of AZ31B wrought magnesium alloy 1 a a,b a a a TAN Wen-da , SHAN Ji-guo* , LEI Xiang , ZHANG Jing , CHEN Wu-zhu , REN Jia-liea aDepartment of Mechanical Engineering, Tsinghua University, Beijing 100084, China bKey Laboratory for Advanced Materials Processing Technology, Ministry of Education, Beijing 100084, China ABSTRACT Sheets of AZ31B wrought magnesium alloy were welded by CO laser. Welds of 2 “partial penetration”, “weld pool penetration”, “keyhole penetration” and “excessive penetration” were obtained, and the “keyhole penetrated” weld possessed the best quality. The light emission of welding plasma was monitored by photo-diode, and it was found that the photo-diode signal varied with different penetration statuses. When the welds were “weld pool penetrated” and “keyhole penetrated”, the average signal amplitude A reached its minimum value. R , which defined as ratio of average amplitude A and standard deviation δ S of signal was introduced to describe the fluctuation tendency of plasma, and the ratio reached its maximum value (which meant the lowest plasma stability) when welds were “weld pool penetrated”. By detecting the minimum valu