覆铝锌板切口防锈处理方法的优选（Optimization of anti rust treatment method for aluminum coated zinc plate incision）.doc

覆铝锌板切口防锈处理方法的优选（Optimization of anti rust treatment method for aluminum coated zinc plate incision） Preferably aluminum zinc plate covered with rust proof treatment method of incision Yan Ming Liu (Zte Corp, Guangdong Shenzhen 518057) [Abstract] introduced aluminum zinc coated plate coating and the corrosion characteristics of incision. The aluminum zinc coated plate cut into corrosion For a variety of incision antirust processing methods to try. Through salt spray test method, screening out the incision antirust treatment way for better comprehensive performance: Silicone rust. [keyword] aluminum zinc coated plate; incision; anti rust treatment; [classification] TG174. [44] B documentcode [1001] article number -1560 (2006) 07 -0066 -03 0 Introduction Aluminum zinc coated plate is B IEC International Inc World College A good product. The special structure of the coating which has excellent Corrosion resistance. Aluminum zinc coated in the normal life of up to 25 A, heat resistance Very good, can be used for high temperature 315 DEG C; and coating film Good adhesion, good processability, punching, shearing can Cutting and welding; surface conductivity is very good, can meet the requirements of electromagnetic shielding Requirement。 Cover the surface of aluminum zinc plate also showed a unique smooth, flat and meticulous Spangle, color is silver, with good appearance. In recent years And with the rapid development of electronic and information industry, aluminum zinc coated plate in electric Device, computer, communications equipment and other electronic products need to external electromagnetic shielding The shell is used more widely. Aluminum zinc coated plate coating is composed of 55% aluminum, 43.4% zinc and 1.6% Silicon composition. Four yuan of crystalline aluminum, zinc, silicon and iron can form dense, The composition of aluminum and zinc aluminum rich dendritic structure, zinc eutectoid Things with them. The corrosion at the beginning of inclusion in the Al