复合工艺（Composite process）.docVIP

复合工艺（Composite process） What is the mechanism of 1, coupling agent? 2, what is the pretreatment of cloth? 1. molecular surface treatment agents generally contain two different groups. Some groups (e.g. silicon alkyl) and inorganic materials (such as glass, metal) on the surface of M - OH chemical reaction to form chemical bond; the other part (such as vinyl groups can react with the resin) to form a chemical bond. The inorganic resin and the nature of these two types of different materials in the form of chemical bond bond together to form a firm whole. 2. the surface treatment agent is added to the sizing (the wetting agent called enhanced wetting agent), in the drawing surface treatment agent is covered in glass fiber. This kind of fiber cloth called pretreatment cloth. 1 main principles, hand lay FRP mold making? A according to the product quantity, shape and size, precision, easy demoulding, molding conditions determine the die material and structure B mould should have sufficient stiffness and strength, C mold surface finish should be higher than the product level is above two The curvature D corner of the die should be increased E shall have integral molding surface porosity, air compressor for large depth due to mold stripping; draft, 2O The f assembling mode and the combination mode, parting surface should be opened in the high surface quality or the power of the body G has a certain heat resistance, heat treatment deformation H light weight, easy material, low cost Release agent handlay up should have what characteristics? (1) no corrosion mold, does not affect the curing resin, and adhesion force; (2) the film fast and smooth; (3) the use of simple, safe, cheap. What are the main raw materials 1, glass steel mold making? What is the 2 glass steel mould adopts the surface mat? 1. (1) gel coat resin (2) surface of the glass fiber felt and glass fiber chopped strand mat 2.A. Enhanced gel, prevent surface cracks; B. The formation of resin rich layer to improve