体外预应力混凝土结构耐久性问题探讨3.pdfVIP

体外预应力混凝土结构耐久性问题探讨 熊学玉 　吴学淑 ( 同济大学 预应力研究所 　上海 　200092) 　　摘 　要 : 分析了体外预应力钢筋的腐蚀机理和混凝土劣化原因 ,在此基础上评述现阶段采取的体外预应 力筋的防腐 、减振措施以及混凝土耐久性的改善措施 。最后 ,结合体外预应力筋的电化学腐蚀原理 ,指出当 前体外预应力混凝土结构在耐久性方面仍存在的问题 ,并提出提高其耐久性的建议 。 　　关键词 : 耐久性 　体外预应力筋 　腐蚀机理 　防腐 　减振 THE STUDY ON THE D URABIL ITY OF EXTERNALLY PRESTRESSED CONCRETE STRUCTURE Xiong Xueyu 　Wu Xueshu (Research Institute of Prestress ,Tongji University 　Shanghai 　200092) Abstract : The corrosion mechanism of externally prestressed tendons and damage mechanism of concrete are analysed. On this basis of analysis ,the measures to prevent the erosion of externally prestressed tendons and to improve the durability of concrete are commented. Finally ,on the basis of electrochemical corrosion mechanism , the limitations of the protection measures are studied and the suggestions to improve the durability of externally prestressed concrete structure are proposed. Keywords : durability 　externally prestressed tendon 　corrosion mechanism 　anticorrosion 　vibration damping 　　国内外统计资料表明 ,耐久性失效是导致混凝 及索的更换 ,可以保证力筋的应力水平及结构的可 土结构在正常使用环境状态下失效的最主要原因之 靠性 ,延长了结构的寿命 ,使其在寿命期内经济性优 一 。预应力混凝土结构的失效不仅会造成巨大的经 于体内预应力混凝土结构 。然而 ,体外预应力结构 济损失 ,甚至还会造成人员伤亡 ,因此必须保证预应 在耐久性方面仍存在问题 ,本文对体外预应力混凝 力混凝土结构的耐久性 。从 20 世纪 50 年代至今 , 土结构的耐久性进行分析 ,在此基础上评述现阶段 体内预应力结构在世界范围内被广泛应用 ,然而 ,体 采取的防护措施 ,指出其仍存在的问题 ,并提出提高 内预应力结构由于预应力筋设置于混凝土内部 , 降 体外预应力混凝土结构耐久性的建议 。 低了混凝土的浇筑质量 ,而且管道灌浆的施工质量 也难以保证 ,这些因素使得体内预应力结构的耐久 1 　体外预应力筋腐蚀破坏原理 性容易出现问题 。英国在对 1958～1977 年修建的 11 　体外预应力筋的基本腐蚀机理 12 座后张混凝土桥梁进行调查发现 ,其中竟有 10 与普通混凝土结构的钢筋腐蚀一样 ,体外预应 座桥的压浆孔道中存在空洞 ; 1996 年 ,英国混凝土 力筋的腐蚀也是一个电化学过程 : 由于预应力筋某