渣铁同出液态精炼渣返炉冶炼钒铁的试验.pdf

1999 年第 4 期 FERRO - ALLOYS 1999 №. 4 总第 147 期 铁 　合 　金 Tot. 147 渣铁同出液态精炼渣返炉冶炼钒铁的试验 白凤仁 (锦州铁合金集团有限责任公司 　锦州 　121005) 摘 　要 　介绍了采用渣铁同出、液态精炼渣返炉冶炼钒铁的工艺试验情况。结果表明 ,该工艺在 技术上可行、工艺上合理 ,克服了我国电硅热法生产钒铁中原固态粉状精炼渣返炉冶炼所存在的 弊端 ,不仅改善了电硅热法冶炼钒铁的技术经济指标 ,而且减轻了其对环境的污染 ,具有较好的经 济效益和社会效益。 关键词 　渣铁混出 　精炼渣 　返回法 　钒铁 　试验 EXPERIMENT OF SMELTING FERROVANADIUM WITH CONCURRENT TAPPING OF SLAG AND IRON AND LIQUID REFINING SLAG RETURNED Bai Fengren (Jinzhou Ferroalloy Group Co. ,Ltd. ,Jinzhou 121005) Abstract 　Experimental status of smelting ferrovanadium with concurrent tapping of slag and iron and liquid refining slag returned is introduced. The result shows that thisprocess was feasible in technology and reasonable in process , the defeats in smelting ferrovanadium with former solid powder refining slag returned furnace were overcome in silicothermic process in China ,not only its technical economic indexes were improved but also its environmental pollution was reduced and economic and social benefit were very well. Keywords Concurrent tapping of slag and iron ,refining slag ,retrun scrap process ,FeV ,experiment 1 　前 　言 由于电硅热法冶炼钒铁最后使用含有 过量五氧化二钒的氧化性炉渣进行精炼 , 因 我国电硅热法冶炼钒铁已有三十多年 此 ,精炼结束后的炉渣钒含量较高 , 一般 V O 为 12 %～17 % ,必须进行回收利用。 的历史 , 生产工艺几经改进 ,技术水平不断 2 5 ( 提高。但是 ,仍存在固态粉状精炼渣返炉的 但是钒铁冶炼的渣铁比较大 精炼渣与合金 问题,影响着钒铁冶炼时间、冶炼电耗及钒 的体积比为2 ∶1) ,势必给精炼渣的返炉回收 回收率等项指标的进一步改善 ,是我国钒铁 带来一系列的麻烦。以往采用渣铁分别出 生产中一直没有解